Efeito de diferentes modelos de envelhecimento na resistência de união em dentina decídua hígida e cariada / Different degradations models to evaluate bond strength in sound and caries primary dentin
São Paulo; s.n; 2015. 90 p. ilus, tab, graf. (BR).
Tesis en Portugués | LILACS, BBO | ID: lil-763788
RESUMO
A resistência de união (RU) dos materiais deve ser avaliada após a degradação da interface adesiva, tentando simular um processo que ocorre naturalmente ao longo do tempo na cavidade bucal. O presente estudo avaliou a degradação da interface adesiva em diferentes materiais utilizando o modelo de envelhecimento in vitro e in situ em dentina hígida e cariada. Noventa segundos molares decíduos hígidos e sem defeitos de esmalte, foram aleatoriamente divididos em dois grupos de acordo com o substrato a ser testado (hígido e com lesão de cárie induzida). A seguir, cada um dos grupos foi subdividido aleatoriamente de acordo com o material restaurador (n=15) resina composta associada ao sistema adesivo - RC, cimento de ionômero de vidro modificado por resina - CIVMR e cimento de ionômero de vidro de alta viscosidade - CIVAV. A superfície da dentina foi preparada e com o auxílio de cânulas de polietileno, foram confeccionados os espécimes com os materiais restauradores. Partes de um mesmo dente foram submetidas a cada envelhecimento in vitro (24 horas e 6 meses) - armazenados em água destilada à 37°C; e in situ (uso de dispositivo intraoral palatino por voluntários em uma fase experimental de 7 dias). Os espécimes foram submetidos ao teste de microcisalhamento (MPa) para avaliação da RU, seguido de análise do padrão de fratura em estereomicroscópio (400X). Os dados foram submetidos a análise de variância de medidas repetidas seguida pelo teste de Bonferroni (? = 5%). De forma geral, o armazenamento por seis meses em água degradou o grupo CIVMR em dentina hígida (<0,001) e RC em dentina cariada (p=0,007), para os outros materiais não houve diferença estatística (p=1,00)...
ABSTRACT
Materials bond strength (BS) should be evaluated after degradation of the adhesive interface, simulating the intra-oral enviroment. This study assessed the degradation of the bonding interface of differents materials using in vitro and in situ models of aging in sound and caries - affected primary dentin. Ninety sound second primary molars without enamel defects were randomly assigned into two groups (sound and induced carious) according to the substrate to be tested. Then each group was subdivided according to the restorative material (n=15) composite resin associated with the adhesive system - CR, resin-modified glass ionomer cement - RMGIC or high-viscous glass ionomer cement- HVGIC. Dentin surface was prepared and with the aid of polyethylene tubes specimens of each restorative materials were prepared. Parts of a same tooth were subjected to in vitro and in situ models of aging. For in vitro model, the specimens were stored in distilled water at 37°C during 24 hours per 6 months; and for in situ model an intraoral palatal device was confectioned and used by volunteers in an experimental phase for 7 days.Specimens were submitted to microshear test (MPa) for BS evaluation and then stereomicroscopy (400X) analys of failure mode. Data were analyzed by repeated measures ANOVA for followed by Bonferroni test (? = 5%). In general, the storage for six months in distilled water degraded the RMGIC group in sound dentin (<0.001) and RC group in caries-affect dentin substrate (p = 0.007), for the others materials there was no statistical difference (p = 1.00)...
Asunto(s)

Texto completo: Disponible Índice: LILACS (Américas) Asunto principal: Diente Primario / Recubrimientos Dentinarios / Cementos de Ionómero Vítreo Tipo de estudio: Ensayo Clínico Controlado Idioma: Portugués Año: 2015 Tipo del documento: Tesis

Similares

MEDLINE

...
LILACS

LIS

Texto completo: Disponible Índice: LILACS (Américas) Asunto principal: Diente Primario / Recubrimientos Dentinarios / Cementos de Ionómero Vítreo Tipo de estudio: Ensayo Clínico Controlado Idioma: Portugués Año: 2015 Tipo del documento: Tesis