Sealing ability of MTA, CPM, and MBPc as root-end filling materials: a bacterial leakage study
J. appl. oral sci
; J. appl. oral sci;24(2): 148-152, Mar.-Apr. 2016. tab, graf
Article
en En
| LILACS
| ID: lil-779904
Biblioteca responsable:
BR1.1
ABSTRACT
ABSTRACT Objectives To evaluate the sealing ability of three root-end filling materials (white MTA, CPM, and MBPc) using an Enterococcus faecalis leakage model. Material and Methods Seventy single-root extracted human teeth were instrumented and root-ends were resected to prepare 3 mm depth cavities. Root-end preparations were filled with white MTA, CPM, and MBPc cements. Enterococcus faecalis was coronally introduced and the apical portion was immersed in BHI culture medium with phenol red indicator. The bacterial leakage was monitored every 24 h for 4 weeks. The statistical analysis was performed using the Wilcoxon-Gehan test (p<0.05). Results All cements showed bacterial leakage after 24 hours, except for the negative control group. The MBPc showed significantly less bacterial leakage compared with the MTA group (p<0.05). No significant differences were found between the CPM and the other groups. Conclusions The epoxy resin-based cement MBPc had lower bacterial leakage compared with the calcium silicate-based cements MTA and CPM.
Palabras clave
Texto completo:
1
Índice:
LILACS
Asunto principal:
Óxidos
/
Materiales de Obturación del Conducto Radicular
/
Silicatos
/
Compuestos de Calcio
/
Compuestos de Aluminio
/
Cementos Dentales
/
Filtración Dental
Tipo de estudio:
Evaluation_studies
/
Prognostic_studies
Límite:
Humans
Idioma:
En
Revista:
J. appl. oral sci
Asunto de la revista:
ODONTOLOGIA
Año:
2016
Tipo del documento:
Article