A STDUY ON THE SURFACE MORPHOLOGY AND BOND STRENGTH OF DENTURE BASE RESIN TO COBALT-CHROMIUM ALLOY AFTER VARYING MODES OF SURFACE TREATMENT / 대한치과보철학회지
The Journal of Korean Academy of Prosthodontics
;
: 78-94, 1997.
Artículo
en Coreano
| WPRIM
| ID: wpr-156407
ABSTRACT
The purpose of this experiment was to determine the effects of various treatments on denture base resin to metal bond for cobalt-chromium alloy. The metal surface was treated as follows. Group 1 Sandblasted with 50microneter aluminum oxide. Group 2 Sandblasted with 250microneter aluminum oxide. Group 3 Sandblasted with 250microneter aluminum oxide and followed by silicoating. Group 4 Electrochemically etched. Group 5 treated with oxidizing solution. Group 6 Beaded with 200microneter retention structure and followed by silicoating. All specimens were applied with 4-META resin and were thermocycled 1000 times at temperature of 5degrees C to 55degrees C. The effects of various surface treatments on the bond strength between 4-META resin and metal interface were measured by using the universal testing machine. All specimens were observed with SEM. The results were as follows 1. The bond strength of 4-META resin were significantly higher to Co-Cr alloy. 2. The bond strength decreased in the following orders group 6, group 3, groups 1 and 2, group 4, group 5 and there was no statistically significant difference in bond strength among groups 1 and 2. (p>0.05) 3. The bond strength of cobalt-chromium alloy to 4-META resin were not significantly different. (p>0.05) 4. The treated surface of groups 1, 2 and 3 has more fine undercut than that of groups 4 and 5 with SEM. 5. Stable adhesion can be achieved when mechanically roughened metal surface by sandblasting than treating in an electrochemical etching and an oxidizing solution with potassium manganate.
Texto completo:
Disponible
Índice:
WPRIM (Pacífico Occidental)
Asunto principal:
Potasio
/
Dentaduras
/
Bases para Dentadura
/
Aleaciones
/
Óxido de Aluminio
Idioma:
Coreano
Revista:
The Journal of Korean Academy of Prosthodontics
Año:
1997
Tipo del documento:
Artículo
Similares
MEDLINE
...
LILACS
LIS