Study of corrosion behavior of titanium with anodized oxidation film / 华西口腔医学杂志
West China Journal of Stomatology
;
(6): 203-205, 2011.
Artículo
en Chino
| WPRIM
| ID: wpr-235086
ABSTRACT
<p><b>OBJECTIVE</b>To investigate the variation of the corrosion resistance of anodized oxidation film on titanium by electrochemical methods.</p><p><b>METHODS</b>TiO2 nanotube layer was formed on Ti surface by anodization. The morphology was observed with scanning electron microscope (SEM) and the crystal phase was analyzed using X-ray diffraction(XRD) before and after annealing. Polarization curves were examined by electrochemical methods.</p><p><b>RESULTS</b>Titanium oxide nanotubes with 80 nm diameter and 400 nm length was seen on Ti after anodization. The annealing nanotubes was anatase crystalline phase by X-ray diffraction analysis. The self-corrosion potential and break-down potential of smooth Ti were significantly lower than TiO2 nanotubes by anodization (P < 0.05). The self-corrosion current and passived current were significantly higher than TiO2 nanotubes by anodization (P < 0.05). Annealing improved the corrosion resistance of anodized oxidation film on titanium.</p><p><b>CONCLUSION</b>The results of electrochemical examinations indicate that the TiO2 nanotubes by anodization increases the corrosion resistance of titanium.</p>
Texto completo:
Disponible
Índice:
WPRIM (Pacífico Occidental)
Asunto principal:
Oxidación-Reducción
/
Titanio
/
Microscopía Electrónica de Rastreo
/
Corrosión
/
Nanotubos
Idioma:
Chino
Revista:
West China Journal of Stomatology
Año:
2011
Tipo del documento:
Artículo
Similares
MEDLINE
...
LILACS
LIS