Effects of air-abrasion pressure on the resin bond strength to zirconia: a combined cyclic loading and thermocycling aging study
Restorative Dentistry & Endodontics
; : 206-215, 2017.
Article
en En
| WPRIM
| ID: wpr-23636
Biblioteca responsable:
WPRO
ABSTRACT
OBJECTIVES: To determine the combined effect of fatigue cyclic loading and thermocycling (CLTC) on the shear bond strength (SBS) of a resin cement to zirconia surfaces that were previously air-abraded with aluminum oxide (Al₂O₃) particles at different pressures. MATERIALS AND METHODS: Seventy-two cuboid zirconia specimens were prepared and randomly assigned to 3 groups according to the air-abrasion pressures (1, 2, and 2.8 bar), and each group was further divided into 2 groups depending on aging parameters (n = 12). Panavia F 2.0 was placed on pre-conditioned zirconia surfaces, and SBS testing was performed either after 24 hours or 10,000 fatigue cycles (cyclic loading) and 5,000 thermocycles. Non-contact profilometry was used to measure surface roughness. Failure modes were evaluated under optical and scanning electron microscopy. The data were analyzed using 2-way analysis of variance and χ² tests (α = 0.05). RESULTS: The 2.8 bar group showed significantly higher surface roughness compared to the 1 bar group (p < 0.05). The interaction between pressure and time/cycling was not significant on SBS, and pressure did not have a significant effect either. SBS was significantly higher (p = 0.006) for 24 hours storage compared to CLTC. The 2 bar-CLTC group presented significantly higher percentage of pre-test failure during fatigue compared to the other groups. Mixed-failure mode was more frequent than adhesive failure. CONCLUSIONS: CLTC significantly decreased the SBS values regardless of the air-abrasion pressure used.
Palabras clave
Texto completo:
1
Índice:
WPRIM
Asunto principal:
Envejecimiento
/
Microscopía Electrónica de Rastreo
/
Adhesivos
/
Cementos de Resina
/
Fatiga
/
Óxido de Aluminio
Idioma:
En
Revista:
Restorative Dentistry & Endodontics
Año:
2017
Tipo del documento:
Article