Micromorphometric Influence of Anodic oxidation surface implant conditioned with tetracycline-HCl / 대한치주과학회지
The Journal of the Korean Academy of Periodontology
;
: 767-777, 2007.
Artículo
en Coreano
| WPRIM
| ID: wpr-24277
ABSTRACT
The present study was performed to evaluate the effect of Tetracycline-HCl on the change of implant surface microstructure according to application time. Anodic oxidation surface were utilized. Implant surface was rubbed with 50mg/ml Tetracycline-HCl solution for 1/2min., 1min., 1 1/2min., 2min., 2 1/2min. and 3min. respectively in the test group. Then, specimens were processed for Ra Value test and scanning electron microscopic observation. The results of this study were as follows. 1. The anodic oxidation surface roughness tests don't show significant difference on conditioning with saline and Tetracycline-HCl. 2. The anodic oxidized surfaces showed the craterous structures. The surface conditioning with Tetracycline-HCl didn't influence on its micro-morphology. In conclusion, Anodic oxidation implant surface is stable to detoxificate with 50mg/ml Tetracycline-HCl of implant surface.
Texto completo:
Disponible
Índice:
WPRIM (Pacífico Occidental)
Idioma:
Coreano
Revista:
The Journal of the Korean Academy of Periodontology
Año:
2007
Tipo del documento:
Artículo
Similares
MEDLINE
...
LILACS
LIS