Influence of soft-start irradiation on polymerization shrinkage stress of universal hybrid composite resins / 中华口腔医学杂志
Chinese Journal of Stomatology
;
(12): 633-636, 2007.
Artículo
en Chino
| WPRIM
| ID: wpr-359672
ABSTRACT
<p><b>OBJECTIVE</b>To compare the difference between soft-start curing mode and standard curing mode in polymerization shrinkage stress of universal hybrid composite resins and to study effect of the soft-start curing mode on the decrease of shrinkage stress.</p><p><b>METHODS</b>Three universal hybrid resins (A Charisma, B TPH Spectrum, and C Esthet-X) were respectively filled in cavities (4 mm in diameter) of epoxide resin disks, 16 specimens of each. Off them, eight of the specimens for each composite resin were exposed using soft-start mode and the other eight using standard mode. Polymerization contraction stress was calculated during 48 h after curing with photo-elastic stress analysis.</p><p><b>RESULTS</b>Three composite resins cured with soft-start mode showed the same trend of shrinkage stress changing as that with standard curing mode and values of polymerization shrinkage stress at 24 h after curing were (3.80 +/- 0.31) MPa, (3.21 +/- 0.40) MPa, and (2.84 +/- 0.22) MPa respectively for A, B and C composite resins. The corresponding figures for the composites with standard curing mode were (4.19 +/- 0.24) MPa, (3.69 +/- 0.33) MPa, and (3.14 +/- 0.28) MPa. Three composite resins cured with soft-start mode had significantly lower polymerization shrinkage stress compared with standard curing mode at 24 h after curing (P < 0.05).</p><p><b>CONCLUSIONS</b>Using soft-start curing mold can reduce, to some extent, the polymerization shrinkage stress of universal hybrid composite resins.</p>
Texto completo:
Disponible
Índice:
WPRIM (Pacífico Occidental)
Asunto principal:
Efectos de la Radiación
/
Resinas Compuestas
/
Análisis del Estrés Dental
/
Luz
Idioma:
Chino
Revista:
Chinese Journal of Stomatology
Año:
2007
Tipo del documento:
Artículo
Similares
MEDLINE
...
LILACS
LIS