A study on fatigue strength of laser welding of titanium and titanium alloy / 实用口腔医学杂志
Journal of Practical Stomatology
;
(6): 463-466, 2009.
Artículo
en Chino
| WPRIM
| ID: wpr-406038
ABSTRACT
Objective:
To investigate the corrosion fatigue strength of laser-welded specimens fabricated from commercially pure titanium (TA2) and titanium alloy(TC4).Methods:
TA2 and TC4 were mechanically processed into a certain size and joined by laser welding. A fatigue testing machine was used to test tensile load and fatigue strength after soaked in synthetic saliva. The fatigue fracture surface was examined by scanning electron microscopy (SEM).Results:
The fatigue strengths of the laser-welded test specimens showed no significant differences compared to specimens in air. SEM examination showed that there were no defects such as corrosion pits.Conclusion:
There are no significant differences between either laser-welded metal in the corrosion fatigue strength for dry specimens and specimens in synthetic saliva.
Texto completo:
Disponible
Índice:
WPRIM (Pacífico Occidental)
Idioma:
Chino
Revista:
Journal of Practical Stomatology
Año:
2009
Tipo del documento:
Artículo
Similares
MEDLINE
...
LILACS
LIS