Nano-hydroxyapatite film as a support to improve the proliferation of human umbilical vein endothelial cells / 中国组织工程研究
Chinese Journal of Tissue Engineering Research
;
(53): 1852-1857, 2015.
Artículo
en Chino
| WPRIM
| ID: wpr-465639
ABSTRACT
BACKGROUND:
A new type of nano-hydroxyapatite artificial mechanical heart valve has been developed using pulsed laser deposition technology at the Department of Materials, Hefei University and Anhui Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, China.OBJECTIVE:
To investigate the compatibility of nano-hydroxyapatite artificial mechanical heart valve with human umbilical vein endothelial cels.METHODS:
Human umbilical vein endothelial cels were in vitroisolated, cultured and passaged to the 2-4 generations, and then the cel suspension was inoculated onto the nano-hydroxyapatite artificial mechanical heart valve. After 3, 7, 12 days of culture, the cel growth on the artificial mechanical heart valve was observed under scanning electron microscope. In addition, the human umbilical vein endothelial cels were respectively cultured in room-temperature and high-temperature extract liquids of nano-hydroxyapatite artificial mechanical heart valve, high-density polyethylene and phenol solution extracts for 72 hours, and then, the proliferation of cels was detected by MTT method. RESULTS ANDCONCLUSION:
Under the scanning electron microscope, the human umbilical vein endothelial cels were fusiform- or polygon-shaped with protuberances adhered to the artificial mechanical heart value at 3 days of culture; the cels were stretched thoroughly and fused at 7 days of culture; and the cels were confluent to pieces that tightly overlaid the heart valve surface and the extracelular matrix was formed localy at 21 days of culture. Results from MTT test displayed that the nano-hydroxyapatite artificial mechanical heart valve had no cytotoxicity to the human umbilical vein endothelial cels, indicating a good cytocompatibility.
Texto completo:
Disponible
Índice:
WPRIM (Pacífico Occidental)
Idioma:
Chino
Revista:
Chinese Journal of Tissue Engineering Research
Año:
2015
Tipo del documento:
Artículo
Similares
MEDLINE
...
LILACS
LIS