The Influence of Surface Roughness of Tooth Preparation and Cement Compatibility on the Adhesive Strength / 天津医药

ABSTRACT

Objective To investigate the influence of tooth preparation surface roughness and different dental ce-ments on adhesive strength, and provide some reference information on the selection of dental rotary instruments and dental cements. Methods Sixty dentin samples were prepared and randomly divided into 3 groups. Samples from group A, B and C were grinded by diamond burs with grit-sizes of 125μm, 60μm and 28μm respectively. Two samples selected randomly from each group were observed under scanning electron microscope (SEM) for the surface microprofile. The remaining 18 samples from each group were evenly divided into 3 subgroups. Each subgroup was teamed with one of 3 dental cementszinc polycarboxylate cement (ZP), glass ionomer cement (GI) and resin-modified glass ionomer cement (RMGI). Co-Cr alloy casts were cemented onto the dentin samples, and the adhesive strength was tested. Meanwhile, the types of failure were re-corded for each sample. Results The surface roughness of tooth preparation samples showed a downward trend in group A, group B and group C. Among the involved 3 dental cements, RMGI exhibited the highest adhesive strength, and there was no significant difference in the adhesive strength between ZP and GI. Among different combination subgroups, A-RMGI had the highest adhesive strength, B-RMGI run the second place, while C-ZP and C-GI were proved the lowest. However, there was no interaction between the two factors. Furthermore, group A mainly showed failure typesⅠandⅡ, group B evenly showed all the failure types and group C mainly showed failure typesⅡandⅢ. Conclusion The adhesive strength is related to the surface roughness. RMGI exhibits the highest adhesive efficiency. There is no obvious compatibility in particular surface roughness and dental cements.