Different fabrication techniques of implant-supported prostheses: microhardness and fracture strength
Braz. j. oral sci
;
18: e191573, jan.-dez. 2019. ilus
Article
Dans Anglais
| LILACS, BBO
| ID: biblio-1095166
ABSTRACT
Aim:
This study evaluated the mechanical behavior of implant-supported crowns obtained by different fabrication technique after thermomechanical cycling.Methods:
Thirty-two external hexagon dental implants were divided into four groups (n=10) CC conventional casting with torch; EI electromagnetic induction casting; PL plasma casting; and CAD-CAM milling through computer-aided design and computer-aided manufacturing. Vickers microhardness of the specimens were made before and after the thermomechanical cycling, and then subjected to fracture load. Fracture pattern was evaluated.Results:
No significant difference was observed comparing the microhardness before and after thermomechanical cycling. CAD-CAM group presented significant lower microhardness than the other groups. No significant statistical difference was showed on fracture load between the groups. The CAD-CAM and PL presented lower number of failure by plastic deformation.Conclusion:
The manufacturing techniques affected the mechanical behavior and the failure pattern of implant-supported crowns tested
Texte intégral:
Disponible
Indice:
LILAS (Amériques)
Sujet Principal:
Prosthodontie
/
Implants dentaires
/
Conception assistée par ordinateur
langue:
Anglais
Texte intégral:
Braz. j. oral sci
Thème du journal:
Dentisterie
Année:
2019
Type:
Article
Pays d'affiliation:
Brésil
Institution/Pays d'affiliation:
Meridional Faculty (IMED)/BR
/
University of Ribeirão Preto/BR
/
University of São Paulo/BR
Documents relatifs à ce sujet
MEDLINE
...
LILACS
LIS