Effect of intrinsic pigmentation on the flexural strength of a microwave-cured acrylic resin
Braz. dent. j
;
13(3): 205-207, 2002. tab
Article
Dans Anglais
| LILACS, BBO
| ID: lil-338545
RESUMO
This study investigated the effect of intrinsic pigmentation on the transverse strength of a microwave-cured acrylic resin. Forty transverse strength specimens were fabricated according to ADA specification #12 and divided into 5 groups. No fibers were added to group I (GI, control group); acrylic stain (AS) was added to GII and GIII in concentrations of 0.5 and 1.5 percent w/w, respectively; acrylic fibers (AF) were added to groups GIV and GV in concentrations of 0.5 and 1.5 percent w/w, respectively. All specimens were irradiated in a microwave oven with a cycle of 3 min at 360 W, followed by 4 min resting, then 3 min at 810 W. Flasks were bench-cooled for 30 min at room temperature, followed by immersion in cold tap water for 30 min. After storage in distilled water at 37ºC for 48 h, all specimens were tested for flexural strength in a testing machine (EMIC-DL 500) at a crosshead speed of 0.5 cm/min. Mean and standard deviation (MPa) for the flexural strength test were GI=86.0 ± 7.9; GII=86.0 ± 9.8; GIII=86.6 ± 7.7; GIV=84.9 ± 5.3; GV=84.9 ± 5.2. No statistical differences were detected among the groups (ANOVA, p>0.05). The addition of the acrylic fibers or the acrylic stain did not affect the transverse strength of the microwave-cured acrylic resin
Texte intégral:
Disponible
Indice:
LILAS (Amériques)
Sujet Principal:
Résines acryliques
/
Conception d'appareil de prothèse dentaire
/
Coloration de prothèse
/
Bases d'appareil de prothèse dentaire
/
Micro-ondes
langue:
Anglais
Texte intégral:
Braz. dent. j
Thème du journal:
Dentisterie
Année:
2002
Type:
Article
Pays d'affiliation:
Brésil
Institution/Pays d'affiliation:
Pontifical Catholic University of Paraná/BR
/
UNICAMP/BR
Documents relatifs à ce sujet
MEDLINE
...
LILACS
LIS