Influência dos fotopolimerizadores (luz halógena X led) na resistência à compressão de resinas compostas / Halogen curing light X led influence on compression resistence of composite resin
Accetta, Danielle Figueiredo; Magalhães Filho, Thalles Ribeiro; Weig, Karin de Mello; Fraga, Ricardo Carvalhaes.
  • Accetta, Danielle Figueiredo; s.af
  • Magalhães Filho, Thalles Ribeiro; s.af
  • Weig, Karin de Mello; s.af
  • Fraga, Ricardo Carvalhaes; Universidade Federal Fluminense. BR
Rev. Fac. Odontol. Porto Alegre ; 49(3): 17-19, 2008. ilus, tab, graf
Article Dans Portugais | LILACS, BBO | ID: lil-563467
RESUMO
O objetivo deste estudo foi verificar a resistência à compressão de três compósitos usados em restaurações diretas (Surefil – Dentsply; Concept – Vigodent; Esthetx – Dentsply) polimerizados através de dois tipos de aparelhos fotopolimerizadores um de luz halógena (Gnatus) e outro de diodo emissor de luz (LED) (Gnatus). Foram confeccionados 30 corpos de prova, sendo 10 para cada material, cada um com 4mm de diâmetro por 6mm de comprimento. Cinco corpos de prova de cada material foram polimerizados com luz halógena e cinco com LED. A manipulação e a polimerização dos materiais foram feitas seguindo as instruções dos fabricantes. Após a confecção, os corpos de prova foram levados à máquina de ensaio (Instron 4204) com carga de 5KN e velocidade de 1,0mm/min para o ensaio da resistência à compressão. Os resultados foram submetidos à análise estatística (ANOVA) e indicaram não haver diferença estatisticamente significante entre as médias.
ABSTRACT
The purpose of this study was to verify the compression resistance of three composites used in direct restorations (Surefil – Dentsply; Concept – Vigodent; Esthetx – Dentsply) polymerized through two types of curing lights halogen (Gnatus) and light emitted diode (LED) (Gnatus). We made 30 bodies of evidence, 10 for each material, with 4mm in diameter by 6mm in length. Five bodies of evidence for each material were polymerized with halogen light and five with LED. The polymerization and manipulation of materials were made following the instructions of manufacturers. After confection, the bodies of evidence were taken from machine test (Instron 4204) with load of 5KN and speed of 1.0mm/min for the test of compression resistance. The results were subjected to statistical analysis (ANOVA) and showed no statistically significant difference between mean.
Sujets)

Texte intégral: Disponible Indice: LILAS (Amériques) Sujet Principal: Résines composites / Résistance à la compression / Instruments dentaires / Restaurations dentaires permanentes langue: Portugais Texte intégral: Rev. Fac. Odontol. Porto Alegre Thème du journal: Dentisterie Année: 2008 Type: Article Pays d'affiliation: Brésil Institution/Pays d'affiliation: Universidade Federal Fluminense/BR

Documents relatifs à ce sujet

MEDLINE

...
LILACS

LIS

Texte intégral: Disponible Indice: LILAS (Amériques) Sujet Principal: Résines composites / Résistance à la compression / Instruments dentaires / Restaurations dentaires permanentes langue: Portugais Texte intégral: Rev. Fac. Odontol. Porto Alegre Thème du journal: Dentisterie Année: 2008 Type: Article Pays d'affiliation: Brésil Institution/Pays d'affiliation: Universidade Federal Fluminense/BR