Influência do tempo de armazenamento na resistência de união à microtração de diferentes sistemas adesivos em dentina superficial e profunda / Influence of water storage time on microtensile bond strength of different adhesive systems on superficial and deep dentin
Braz. dent. sci
;
13(1/2): 16-22, 2010. tab
Article
Dans Portugais
| LILACS, BBO
| ID: lil-642686
RESUMO
O objetivo deste estudo foi avaliar a resistência de união (RU) de um sistema adesivo convencional (Adper Single Bond 2 [SB] (3M ESPE, St. Paul, MN, EUA)) e de dois autocondicionantes (Adper SE Plus [SE] (3M ESPE, St. Paul, MN, EUA) e AdheSE® [AD] (Ivoclar Vivadent, Schaan, Liechtenstein, DDR)) em dentina superficial (DS) e profunda (DP), nos tempos imediatamente e após 6 meses de armazenamento em água. Superfícies oclusais de 24 terceiros molares humanos foram seccionadas e smear layer padronizada. Após procedimentos adesivos, as superfícies dos dentes receberam restaurações em resina composta. Tais dentes foram seccionados obtendo-se espécimes em forma de palitos (0,7 + 0,1mm2). Os espécimes foram testados por meio do ensaio de microtração (0,5 mm/min), imediatamente e após 6 meses de armazenamento em água. Os dados foram submetidos à ANOVA 3 fatores e ao pós-teste de Bonferroni (α=0,05). Na avaliação imediatamente da RU, apenas o fator adesivo foi significativo (p<0,05). Os dados de RU após 6 meses mostraram que a interação dos fatores adesivo e substrato dentinário foi significativa (p<0,05). AD em DS (IM 49,0 ± 6,7 MPa) mostrou diminuição significativa da RU após 6M (23,2 ± 7,9 MPa) de armazenamento em água. SE e AD mostraram diferença significativa (p<0,05) tanto em DS como em DP. Em DS o fator tempo foi significativo e em DP o fator adesivo foi significativo. SB tanto em DS como em DP não apresentou diferença estatisticamente significante imediatamente e após 6 meses (p>0,05). Conclui-se que diferentes níveis de profundidade dentinária podem afetar a RU para o mesmo material e que o fator tempo pode influenciar a degradação do sistema adesivo.
ABSTRACT
The aim of this study was to evaluate the resin-dentin bond strengths (μTBS) of a total-etch adhesive system (Adper Single Bond 2 [SB], 3M ESPE, St. Paul, MN, USA) and of two self-etch adhesive systems (Adper SE Plus [SE], 3M ESPE, St. Paul, MN, USA and AdheSE® [AD], Ivoclar Vivadent, Schaan, Liechtenstein, DDR) in superficial dentin (SD) and deep dentine (DD) immediately and after 6 months of storage in water. Surface occlusals of 24 carie-free human third molars were exposed to their SD or DD and polished to create a standardized smear layer. After the adhesive procedures, composite buildups were constructed incrementally and sectioned to obtain bonded sticks (0.7 + 0.1 mm2) that were tested in tension (0.5 mm/min) immediately and after 6 months of water storage. The μTBS data were submitted to a three--way analysis of variance (ANOVA) model with Bonferroni tests (α=0.05). In the evaluation of the immediate μTBS, only the adhesive factor was significant (p <0.05). After 6 months of storage in water, the interaction of the adhesive and dentinal substrate factors was significant (p<0.05). The AD in SD (IM 49.0 ± 6.7 MPa) showed a significant decrease in the μTBS after 6 months of storage in water (23.2 ± 7.9 MPa). The SE and AD showed a significant difference (p<0.05) in the SD and DD. The most significant factor for the SD was time, while for the DD, it was the adhesive. The SB in the SD and DD showed no statistically significant differences either immediately or after 6 months (p> 0.05). In conclusion, different levels of dentin depth can affect the bond strength for the same material, and time may influence the degradation of the adhesive system.
Texte intégral:
Disponible
Indice:
LILAS (Amériques)
Sujet Principal:
Résistance à la traction
/
Agents de collage dentinaire
/
Dentine
Type d'étude:
Étude pronostique
Limites du sujet:
Humains
langue:
Portugais
Texte intégral:
Braz. dent. sci
Thème du journal:
Dentisterie
/
Sa£de Bucal
Année:
2010
Type:
Article
Pays d'affiliation:
Brésil
Institution/Pays d'affiliation:
Universidade Estadual de Ponta Grossa/BR
Documents relatifs à ce sujet
MEDLINE
...
LILACS
LIS