Surface roughness and wear of resin cements after toothbrush abrasion
Braz. oral res. (Online)
;
29(1): 1-5, 2015. tab, ilus
Article
Dans Anglais
| LILACS
| ID: lil-777244
ABSTRACT
Increased surface roughness and wear of resin cements may cause failure of indirect restorations. The aim of this study was to evaluate quantitatively the surface roughness change and the vertical wear of four resin cements subjected to mechanical toothbrushing abrasion. Ten rectangular specimens (15 × 5 × 4 mm) were fabricated according to manufacturer instructions for each group (n = 10) Nexus 3, Kerr (NX3); RelyX ARC, 3M ESPE (ARC); RelyX U100, 3M ESPE (U100); and Variolink II, Ivoclar/Vivadent (VL2). Initial roughness (Ra, µm) was obtained through 5 readings with a roughness meter. Specimens were then subjected to toothbrushing abrasion (100,000 cycles), and further evaluation was conducted for final roughness. Vertical wear (µm) was quantified by 3 readings of the real profile between control and brushed surfaces. Data were subjected to analysis of variance, followed by Tukey’s test (p < 0.05). The Pearson correlation test was performed between the surface roughness change and wear (p < 0.05). The mean values of initial/final roughness (Ra, µm)/wear (µm) were as follows NX3 (0.078/0.127/23.175); ARC (0.086/0.246/20.263); U100 (0.296/0.589/16.952); and VL2 (0.313/0.512/22.876). Toothbrushing abrasion increased surface roughness and wear of all resin cements tested, although no correlation was found between those variables. Vertical wear was similar among groups; however, it was considered high and may lead to gap formation in indirect restorations.
Texte intégral:
Disponible
Indice:
LILAS (Amériques)
Sujet Principal:
Abrasion dentaire
/
Brossage dentaire
/
Céments résine
/
Restauration d'usure occlusale
langue:
Anglais
Texte intégral:
Braz. oral res. (Online)
Thème du journal:
Dentisterie
Année:
2015
Type:
Article
/
descriptif de projet
Pays d'affiliation:
Brésil
Institution/Pays d'affiliation:
Universidade de São Paulo/BR
Documents relatifs à ce sujet
MEDLINE
...
LILACS
LIS