Effect of Surface Treatment of Two Ceramic Materials by Er, Cr:YSGG Laser Irradiation on The Shear Bond Strength to Resin Cement: "a Comparative in-Vitro Study" / Efeito do tratamento de superfície de dois materiais cerâmicos por Irradiação de laser Er, Cr:YSGG na resistência ao cisalhamento a cimento Resinoso: "um estudo comparativo in-Vitro"

ABSTRACT

Objective: The aim of this study is to assess the effect of Er,CrYSGG laser on the shear bond strength (SBS) and surface topography of two CAD/CAM ceramic materials bonded with self adhesive resin cement. Material and methods: sixty ceramic CAD/CAM discs were obtained, 30 lithium disilicate (IPS Emax) (Group LD), and 30 hybrid resin ceramic (Vita Enamic) (Group RC). The Slices were allocated into six groups (n=10) according to ceramic material and surface treatment; Group (LD-C) IPS Emax treated with 9% hydrofluoric acid (HF), Groups (LD-L1) and (LD-L2) IPS Emax treated with Er,CrYSGG, Group (RC-C) Vita Enamic treated with 9% hydrofluoric acid (HF), Groups (RC-L1) and (RC-L2) Vita Enamic treated with Er,CrYSGG laser. The laser parameters and irradiation protocol was 1.5 W (L1) and 2.5 W (L2). All samples were cemented with self-adhesive resin cement and thermocycled for 5000 cycles. The SBS was measured using a universal testing machine and the mean values (MPa) were analyzed using Two-way (ANOVA) (P ≤ 0.05) and Bonferroni's post-hoc test. Results: RC-C (16.55) showed highest SBS followed by LD-C (13.79), which revealed no statistically significant difference with RCP1 (12.33) and RC-P2 (11.2). The lowest SBS values were found with LD-P1 (2.7) and LDP2 (2.1). SEM analysis revealed Vita Enamic to have the highest surface roughness. Fracture pattern analysis showed adhesive failure with IPS Emax groups and mixed failure with Vita Enamic groups. Conclusion: Er,CrYSGG laser irradiation with the parameters used did not increase SBS of IPS Emax and Vita Enamic with composite resin compared to HF acid etching (AU)

RESUMO

Objetivo: O objetivo deste estudo é avaliar o efeito do laser Er,CrYSGG na resistência ao cisalhamento (SBS) e na topografia superficial de dois materiais cerâmicos CAD/CAM cimentados com cimento resinoso autoadesivo. Material e métodos: foram obtidos sessenta discos cerâmicos CAD/CAM, 30 de dissilicato de lítio (IPS Emax) (Grupo LD) e 30 de resina híbrida (Vita Enamic)(Grupo RC). Os discos foram alocados em seis grupos (n = 10), de acordo como material cerâmico e o tratamento de superfície; Grupo (LD-C) IPS Emaxtratado com ácido fluorídrico (HF) a 9%, Grupos (LD-L1) e (LD-L2) IPS Emaxtratado com Er,CrYSGG, Grupo (RC-C) Vita Enamic tratada com ácido fluorídrico (HF) a 9%, Grupos (RC-L1) e (RC-L2) Vita Enamic tratada com laser Er,CrYSGG. Os parâmetros do laser e o protocolo de irradiação foram de 1,5 W (L1) e 2,5 W (L2). Todas as amostras foram cimentadas com cimento resinoso autoadesivo e termocicladas por 5000 ciclos. A SBS foi medida usando uma máquina de ensaios universais e os valores médios (MPa) foram analisados usando (ANOVA) a dois fatores (P ≤ 0,05) e teste post-hoc de Bonferroni. Resultados: RC-C (16,55) apresentou maior SBS seguido por LD-C (13,79), que não revelou diferença estatisticamente significante com RCP1(12,33) e RC-P2 (11,2). Os menores valores de SBS foram encontrados comLD-P1 (2,7) e LD-P2 (2,1). A análise por MEV revelou que a Vita Enamic possui maior rugosidade de superfície. A análise do padrão de fratura mostrou falha adesiva nos grupos IPS Emax e falha mista nos grupos Vita Enamic. Conclusão: A irradiação com laser Er,CrYSGG com os parâmetros utilizados não aumentou a SBS de IPS Emax e Vita Enamic ao cimento resinoso em comparação com o condicionamento ácido com HF.(AU)