The effects of heating on the physicochemical properties of tricalcium silicate root canal sealers

ABSTRACT

Abstract This study evaluated the effect of heating on the physicochemical properties and surface changes of tricalcium silicate sealers. Three tricalcium silicate root canal sealers (Bio-C Sealer, BioRoot-RCS, EndoSequence BC Sealer), and one epoxy resin-based sealer (AH Plus; control) were tested. The effect of heating on setting time (ST) and flowability were assessed according to ANSI/ADA 57 and ISO 6876 standards. Solubility and dimensional change (DC) of the set sealers were evaluated at 24 hours and after 30 days; the pH of the water used in the DC testing was also measured. Tests were repeated with heated sealers in an oven at 100 °C for 1 min. SEM and EDS analysis were performed. Data were analyzed using One-Way ANOVA and Tukey post-hoc tests (α=5%). Heating decreased the ST for AH Plus and EndoSequence (p<0.05). Heating reduced flowability (p<0.05) and increased pH for AH Plus (p<0.05). The solubility of Bio-C (dried specimens) was not in accordance with the ANSI/ADA standard. The solubility of EndoSequence was significantly higher (p<0.05) when it was heated and dried after 30 days. DC of Bio-C (24 h and 30 days), BioRoot-RCS (30 days) and AH Plus (24 h and 30 days) were not in accordance with the standards. SEM and EDS analysis showed significant changes in sealer microstructure after heating. In conclusion, heating decreased the ST and increased the solubility of EndoSequence BC sealer. No significant changes in flowability, DC, and pH were identified for all three tricalcium silicate sealers after heat application. However, all sealers had significant surface changes.

RESUMO

Resumo Este estudo avaliou o efeito do aquecimento nas propriedades físico-químicas e nas alterações superficiais de cimentos de silicato tricálcico. Três cimentos endodônticos de silicato tricálcico (Bio-C Sealer, BioRoot-RCS, EndoSequence BC Sealer) e um cimento à base de resina epóxi (AH Plus) foram testados para avaliar o efeito do aquecimento no tempo de presa (TP) e escoamento de acordo com as normas ANSI/ADA 57 e ISO 6876. A solubilidade e alteração dimensional (AD) dos cimentos foram avaliadas após 24 horas e 30 dias. O pH da água usada no teste de AD também foi medido. Os testes foram repetidos com cimentos aquecidos em um forno a 100 °C por 1 min. Análises em MEV e EDS foram realizadas. Os dados foram analisados pelos testes de ANOVA-1 via e post hoc de Tukey (α=5%). O aquecimento diminuiu o TP para AH Plus e EndoSequence (p<0,05). O aquecimento reduziu o escoamento (p<0,05) e aumentou o pH do AH Plus (p<0,05). A solubilidade do Bio-C (amostras desidratadas) não estava de acordo com o padrão ANSI/ADA. A solubilidade da EndoSequence foi significativamente maior (p<0,05) quando aquecida e desidratada após 30 dias. As AD de Bio-C (24 h e 30 dias), BioRoot-RCS (30 dias) e AH Plus (24 h e 30 dias) não estavam de acordo com as normas ADA e ISO. A análise em MEV e EDS mostrou alterações significativas na estrutura dos cimentos após aquecimento. Em conclusão, o aquecimento diminuiu o TP e aumentou a solubilidade do cimento EndoSequence BC. Não foram identificadas mudanças significativas no escoamento, AD e pH para os cimentos de silicato tricálcico após aquecimento. Porém, todos os cimentos tiveram alterações significativas na superfície.