Filmes de SiOx crescidos em substrato de Zircônia tetragonal policristalina estabilizada por ítria: influência na durabilidade da adesão a cimentos resinosos / SiOx films growth on Y-TZP: influence on adhesion to resin cements
São José dos Campos; s.n; 2011. 129 p. ilus, tab, graf.
Tese em Português | LILACS, BBO | ID: biblio-866977
RESUMO
Este estudo comparou o efeito de filmes à base de Si depositados pela técnica reactive magnetron sputtering com o uso do jateamento de partículas de alumina e a aplicação de primer na adesão de cimentos resinoso a superfície de zircônia. Blocos de zirconia (N=300) (4,5¡¿4,5)mm foram sinterizados e regularizados com lixas de SiC (1200), sonicamente limpos com água destilada por 10 min e randomicamente divididos em 30 grupos (n=10) de acordo com 3 parâmetros 1- cimento resinoso (Panavia/Kuraray; Multilink/Ivoclar; RelyX U100/3M); 2- tratamento de superfície (sem tratamento controle, Metal/Zirconia Primer, jateamento com partículas +Metal/Zirconia Primer, Filme A + Monobond S; Filme B + MonobondS); 3- termociclagem (TC). Parâmetros de rugosidade da superfície (Ra, Rz, Sdr) foram avaliados por Microscopia de Interferência e Microscopia Eletrônica de Varredura (MEV). Cilindros de cimento resinoso foram construídos (¨ª 2,4 mm; altura 2 mm) sobre asuperfície de zirconia. O ensaio de resistência adesiva ao cisalhamento foi realizado no momento inicial (24 h) e após a termociclagem (5o-55 oC, 6.000 ciclos) utilizando máquina de ensaio universal (1 mm/min). As superfícies fraturadas foram analisadas por microscopia ótica (30¡¿) e MEV (100¡¿ e 2000¡¿) para categorizar o modo de falha. Adicionais blocos de zirconia (15¡¿15)mm confeccionados para análises por Espectroscopia por Retroespalhamento de Rutheford (RBS), e Trabalho de Adesão (WA) após os tratamentos de superfície. Os dados foram estatisticamente analisados por Anova 3-fatores e teste Tukey (5%). Fotomicrografias revelaram microdefeitos nos filmes. Os resultados de Wa mostraram que os filmes melhoraram a molhabilidade da superfície. As análises por RBS mostraram que a concentração elementar dos filmes variou de acordo com os parâmetros de deposição utilizados nessa pesquisa. O tratamento por jateamento de partículas produzio os maiores valores para os diferentes parâmetros de rugosidade diferentes...
ABSTRACT
This study compared the effectjavascriptvoid(Set_Locked(0,'GRAVA REGISTRO/COMPLEMENTO.x')) of si-based nanofilm deposition usingreactive magnetron sputtering to application of air-abrasion (aluminaparticles) and zirconia primers on the adhesion of resin cements to zirconia. Zirconia (Nblocks=300) (4.5 mm ¡¿ 3.5 mm ¡¿ 4.5 mm) were sintered, ground finished to 1200 SiC paper and cleaned ultrasonically in distilled water for 10 min. The blocks were randomlydivided into 30 groups (n=10) according to 3 testing parameters 1-Resin Cements (Panavia/Kuraray; Multilink/Ivoclar; RelyX U100/3M); 2- Surface conditioning (no conditioning-control, Metal/Zirconia Primer, air-abrasion + Metal/Zirconia Primer, Sibased film A + Monobond S; Si-based film B + Monobond S); 3- Aging (with and without). Surface roughness parameters (Ra, Rz, Sdr) before and after surface conditioning were evaluated using interference microscopy (IM). Rutheford Backscattering Spectroscopy (RBS), Scanning Electron Microscopy (SEM), and Work of Adhesion(WA) analyses were performed after surface treatments. Resin cementswere incrementally built up (¨ª 2.4 mm; height 4 mm) on the zirconia surfaces. Bonded specimens were then thermocycled (5o-55oC, 6,000 cycles). Shear bond strength (SBS) was performed using the Universal Testing Machine (1 mm/min). After fracture, the surfaces were analyzed using an optical microscopy (30 ¡¿), SEM (100 ¡¿ and 2000 ¡¿) to categorize the failure modes. The data were statistically evaluated using 3-way ANOVA and Tukey's test (5%). Scanning Electron Microscopy showed micro defects on Si-based nanofilms surface. The result to Wa showed that surface coated with Si-based nanofilms improved wetability when compared to the other surface treatments. RBS analysis showed that was produced films with different chemical elemental concentration. While air-abraded zirconia surfaces presented the highest roughness parameters (Ra 0.57 nm ¡¾ 0.1, Rz 6.2 ¥ìm ¡¾ 0.2, Sdr 80.4% ¡¾ 4.9), non-conditioned....
Assuntos

Texto completo: DisponíveL Índice: LILACS (Américas) Assunto principal: Plasma / Zircônio / Teste de Materiais / Dióxido de Silício / Cimentos de Resina / Abrasão Dental por Ar / Resistência ao Cisalhamento Tipo de estudo: Ensaio Clínico Controlado Idioma: Português Ano de publicação: 2011 Tipo de documento: Tese

Similares

MEDLINE

...
LILACS

LIS

Texto completo: DisponíveL Índice: LILACS (Américas) Assunto principal: Plasma / Zircônio / Teste de Materiais / Dióxido de Silício / Cimentos de Resina / Abrasão Dental por Ar / Resistência ao Cisalhamento Tipo de estudo: Ensaio Clínico Controlado Idioma: Português Ano de publicação: 2011 Tipo de documento: Tese