Avaliação da resistência ao deslocamento na sobreposição de fios de níquel e titânio superelásticos termoativados em braquetes autoligáveis passivos / Assessment of the displacement resistance of overlapped heat-activated superelastic nickel titanium wires in passive self-ligating brackets

RESUMO

Objetivos: O objetivo desta pesquisa foi comparar a resistência ao deslocamento de fios de níquel e titânio superelásticos termoativados sobrepostos, em braquetes ortodônticos metálicos autoligáveis passivos. Material e Métodos: Foram utilizadas três espessuras de fios de níquel e titânio superelásticos termoativados (NiTi-TA): 0,014 sobreposto ao 0,016 e 0,020 (FlexyNiTi Thermal - Orthometric, Marília, SP, BR), associados a dois tipos de braquetes metálicos autoligáveis passivos: SmartClip SL3® (3M Unitek, Monrovia, CA, EUA) e OrthoClip SLB® (Orthometric, Marília, SP, BR). Um dispositivo que continha 5 braquetes de cada tipo (do incisivo central superior direito ao 2º pré-molar superior direito) foi desenvolvido para realização dos testes. O braquete do canino foi colado em uma barra de aço inoxidável móvel que permitia alterar sua posição vertical, enquanto os demais braquetes foram colados a uma barra fixa de acrílico. As forças obtidas por meio do deslocamento vertical do braquete do canino de 0mm para 1,5mm, 3,0 mm, 4,5mm e 6,0 mm foram registradas. O ambiente de teste foi seco com temperatura controlada de 36,5º C ± 1º C. Um total de 160 testes foi realizado na máquina de ensaios universal Instron. Os testes estatísticos de Shapiro-Wilk, teste t de Student não pareado e ANOVA com testes post-hoc de Tukey foram aplicados aos dados (p<0,05). Resultados: A distribuição normal da amostra foi confirmada, e os testes paramétricos demonstraram que houve diferenças estatisticamente significativas no braquete SmartClip SL3® quando associados aos fios de NiTi-TA 0,020 e 0,014 sobreposto ao 0,016 nas alturas de 1,5mm (p=0,003) e 6mm (p0,0001).

ABSTRACT

Objective: The objective of this research was to compare the displacement resistance of overlapped heat-activated superelastic nickel titanium wires, in passive self-ligating metallic brackets. Material and Methods: Three thicknesses of heat-activated superelastic nickel titanium wires (NiTi-TA) were used: 0.014 overlapped with 0.016 and 0.020 (FlexyNiTi Thermal - Orthometric, Marília, SP, BR), associated with two types of passive self-ligating metallic brackets: SmartClip SL3® (3M Unitek, Monrovia, CA, EUA) and OrthoClip SLB® (Orthometric, Marília, SP, BR). A device with 5 brackets of each type (from right central incisor to the second maxillary premolar) was developed for this research. The canine bracket was attached to a sliding stainless steel bar which allowed the alteration of its vertical position, while the remaining brackets were attached to a fixed acrylic bar. The forces generated by means of the canine bracket vertical displacement from 0mm to 1.5mm; 3.0mm; 4.5mm and 6.0mm were recorded. The test environment was dry with a controlled temperature of 36.5º C ± 1º C. A total of 160 tests were carried out in the Instron Testing Machine. The Shapiro-Wilk test, non-paired Student t-test and ANOVA with Tukey post hoc test were applied to the data (p<0.05). Results: The normal distribution was confirmed, and the parametric tests showed that there were statistically significant differences in the SmartClip SL3® when associated with the NiTi-TA 0.020 and 0.014 wires overlapped to the 0.016 wire in the height of 1.5mm (p=0.003) and 6mm (p<0.0001). However, statistically significant differences were not found in the heights of 3mm (p=0.76) and 4.5mm (p=0.09). For the OrthoClip SLB® brackets, there were statistically significant differences between the NiTi-TA 0.020 and 0.014 wires overlapped with the 0.016 wire in all the heights assessed (p<0.0001).