Bond strength between a polymer-infiltrated ceramic network and a composite for repair: effect of several ceramic surface treatments
Braz. oral res. (Online)
;
32: e28, 2018. tab, graf
Artigo
em Inglês
| LILACS
| ID: biblio-889483
ABSTRACT
Abstract: The effects of several ceramic surface treatments on bond strength of a polymer-infiltrated ceramic network and resin composite as repair material were evaluated. CAD-CAM blocks of a polymer-infiltrated ceramic network (Vita Enamic) were sliced and subjected to aging process, followed by embedding in acrylic resin. The bonding/repair area was treated as follows (n = 30): C- without treatment; UA- universal adhesive application; FM- 10% hydrofluoric acid and silane application; OM-airborne-particle abrasion with aluminum oxide and silane application; RP- tribochemical silica coating; and CA- surface grinding and application of universal adhesive. Composite resin cylinders were made on the treated surface. Specimens from each group were assigned randomly to two subgroups (n = 15) considering storage condition: Baseline (shear tests after 48 hours) or Storage (tests after 6 months under distilled water). The treated surfaces were analyzed by goniometry, roughness, and SEM. Two-way ANOVA and 1-way ANOVA were applied to analyze the bond data and roughness / contact angle data, respectively, followed by Tukey's test (α = 5%). Surface treatments and storage conditions affected bond strengths (p < 0.01). Surface grinding (CA) followed by universal adhesive promoted the highest value of bond strength (14.5 ± 4.8 MPa for baseline, 8.5 ± 3.4 MPa for storage) and the roughest ceramic surface. Grinding with silicon carbide paper (simulating diamond bur) followed by the application of a universal adhesive system is the best option for repairing fractures of the polymer-infiltrated ceramic network.
Texto completo:
DisponíveL
Índice:
LILACS (Américas)
Assunto principal:
Polímeros
/
Cerâmica
/
Colagem Dentária
/
Resinas Compostas
Tipo de estudo:
Estudos de avaliação
Idioma:
Inglês
Revista:
Braz. oral res. (Online)
Assunto da revista:
Odontologia
Ano de publicação:
2018
Tipo de documento:
Artigo
País de afiliação:
Brasil
Instituição/País de afiliação:
Universidade Estadual Paulista - Unesp/BR
Similares
MEDLINE
...
LILACS
LIS