ABSTRACT
Abstract This in vitro study evaluated the fatigue strength of different ceramic materials indicated for monolithic restorations. Disc-shaped specimens were made according to ISO 6872 from five different ceramic materials: feldspathic ceramic (FC), polymer-infiltrated ceramic network (PIC), lithium disilicate glass-ceramic (LD), zirconia-reinforced lithium silicate glass-ceramic (ZLS), and high translucent tetragonal zirconia polycrystals doped by yttrium (YZ-HT). After obtaining the mean of each material (n = 5) from monotonic load-to-failure tests, specimens (n = 20) were subjected to fatigue tests (staircase method) using a biaxial flexural setup (piston-on-three-balls), to determine the fatigue strength. The parameters used for fatigue tests were: 100,000 cycles at 10 Hz, initial load of ~ 60% of mean load-to-failure, and step size of 5% of the initial load (specific for each ceramic material). Kruskal-Wallis and Bonferroni's test (α = 0.05) were used to analyze the fatigue strength data. Fatigue strength (MPa) of the materials was statistically different among each other as follows: YZ-HT (370.2 ± 38.7) > LD (175.2 ± 7.5) > ZLS (152.1 ± 7.5) > PIC (81.8 ± 3.9) > FC (50.8 ± 1.9). Thus, it can be concluded that, in terms of fatigue, high translucent polycrystalline zirconia is the best choice for monolithic restorations as it bears the highest load before cracking/fracturing.
Texto completo:
DisponíveL
Índice:
LILACS (Américas)
Assunto principal:
Estresse Mecânico
/
Cerâmica
/
Desenho Assistido por Computador
/
Falha de Restauração Dentária
Tipo de estudo:
Estudos de avaliação
Idioma:
Inglês
Revista:
Braz. oral res. (Online)
Assunto da revista:
Odontologia
Ano de publicação:
2018
Tipo de documento:
Artigo
País de afiliação:
Brasil
Instituição/País de afiliação:
Universidade Estadual Paulisa/BR
/
Universidade Federal de Santa Maria/BR
/
Universidade de Taubaté/BR
Similares
MEDLINE
...
LILACS
LIS