Effect of intrinsic pigmentation on the flexural strength of a microwave-cured acrylic resin
Silva, Frederico Augusto Peixoto; Silva, Tatiana Bernardon Peixoto; Del Bel Cury, Altair Antoninha; Rached, Rodrigo Nunes.
  • Silva, Frederico Augusto Peixoto; UNICAMP. Dental School of Piracicaba. Department of Prosthodontics and Periodontology. Piracicaba. BR
  • Silva, Tatiana Bernardon Peixoto; UNICAMP. Dental School of Piracicaba. Department of Prosthodontics and Periodontology. Piracicaba. BR
  • Del Bel Cury, Altair Antoninha; UNICAMP. Dental School of Piracicaba. Department of Prosthodontics and Periodontology. Piracicaba. BR
  • Rached, Rodrigo Nunes; Pontifical Catholic University of Paraná. School of Dentistry. Department of Dental Materials. Curitiba. BR
Braz. dent. j ; 13(3): 205-207, 2002. tab
Artigo em Inglês | LILACS, BBO | ID: lil-338545
RESUMO
This study investigated the effect of intrinsic pigmentation on the transverse strength of a microwave-cured acrylic resin. Forty transverse strength specimens were fabricated according to ADA specification #12 and divided into 5 groups. No fibers were added to group I (GI, control group); acrylic stain (AS) was added to GII and GIII in concentrations of 0.5 and 1.5 percent w/w, respectively; acrylic fibers (AF) were added to groups GIV and GV in concentrations of 0.5 and 1.5 percent w/w, respectively. All specimens were irradiated in a microwave oven with a cycle of 3 min at 360 W, followed by 4 min resting, then 3 min at 810 W. Flasks were bench-cooled for 30 min at room temperature, followed by immersion in cold tap water for 30 min. After storage in distilled water at 37ºC for 48 h, all specimens were tested for flexural strength in a testing machine (EMIC-DL 500) at a crosshead speed of 0.5 cm/min. Mean and standard deviation (MPa) for the flexural strength test were GI=86.0 ± 7.9; GII=86.0 ± 9.8; GIII=86.6 ± 7.7; GIV=84.9 ± 5.3; GV=84.9 ± 5.2. No statistical differences were detected among the groups (ANOVA, p>0.05). The addition of the acrylic fibers or the acrylic stain did not affect the transverse strength of the microwave-cured acrylic resin
Assuntos
Texto completo: DisponíveL Índice: LILACS (Américas) Assunto principal: Resinas Acrílicas / Planejamento de Dentadura / Pigmentação em Prótese / Bases de Dentadura / Micro-Ondas Idioma: Inglês Revista: Braz. dent. j Assunto da revista: Odontologia Ano de publicação: 2002 Tipo de documento: Artigo País de afiliação: Brasil Instituição/País de afiliação: Pontifical Catholic University of Paraná/BR / UNICAMP/BR

Similares

MEDLINE

...
LILACS

LIS

Texto completo: DisponíveL Índice: LILACS (Américas) Assunto principal: Resinas Acrílicas / Planejamento de Dentadura / Pigmentação em Prótese / Bases de Dentadura / Micro-Ondas Idioma: Inglês Revista: Braz. dent. j Assunto da revista: Odontologia Ano de publicação: 2002 Tipo de documento: Artigo País de afiliação: Brasil Instituição/País de afiliação: Pontifical Catholic University of Paraná/BR / UNICAMP/BR