Evaluation of solubility, disintegration, and dimensional alterations of a glass ionomer root canal sealer
Braz. dent. j
;
14(2): 114-118, 2003. tab
Artigo
em Inglês
| LILACS
| ID: lil-347122
RESUMO
The aim of this study was to evaluate the glass ionomer cement Ketac-Endo (K) compared with Endofill (E), N-Rickert (N), and Sealer 26 (S) in terms of disintegration, solubility, and dimensional alteration properties, based on ADA Specification No 57. For dimensional alterations, 12-mm high cylindric specimens measuring 6 mm in diameter were prepared and left to stand for a period corresponding to three times the setting time. These specimens were immersed in 30 ml of deionized distilled water after measuring their length with a caliper. Thirty days later, the sample was removed from the container, dried and measured again for length to determine the percent of dimensional alteration. For solubility and disintegration, 1.5-mm thick cement samples measuring 20 mm in diameter were prepared and left to stand for a period corresponding to three times the setting time. The samples were weighed and immersed in 50 ml of deionized distilled water. After seven days, the samples were removed, dried and weighed again to determine the mass loss of each sample, expressed as percentage of original mass. This was considered to correspond to solubility and disintegration of cement. The results were dimensional alteration E (+0.14), K (-0.24), N (+0.23), S (+3.26); for disintegration and solubility E (3.90), K (9.90), N (3.00), S (0.25). We concluded that the dimensional alteration of all cements conformed to ADA standards; Endofill and Ketac-Endo sealers presented higher values for disintegration and solubility than ADA recommendations. Obturating a root canal with a sealer that presents low disintegration and low contraction could minimize the penetration of fluids into the root canal system, thus sealing the space hermetically
Texto completo:
DisponíveL
Índice:
LILACS (Américas)
Assunto principal:
Materiais Restauradores do Canal Radicular
/
Cimentos de Ionômeros de Vidro
Tipo de estudo:
Estudos de avaliação
Idioma:
Inglês
Revista:
Braz. dent. j
Assunto da revista:
Odontologia
Ano de publicação:
2003
Tipo de documento:
Artigo
/
Documento de projeto
País de afiliação:
Brasil
Instituição/País de afiliação:
UNICAMP/BR
/
University of Ribeirão Preto/BR
/
University of São Paulo/BR
Similares
MEDLINE
...
LILACS
LIS