Avaliação in vitro da resistência ao cisalhamento e liberação de flúor de dois cimentos de ionômero de vidro reforçado por resina / In vitro evaluation of shear bond strength and fluoride release from two resin-reinforced glass ionomer cements
Rev. odonto ciênc
;
22(58): 305-310, out.-dez. 2007. graf, ilus, tab
Artigo
em Português
| LILACS
| ID: lil-487209
RESUMO
O objetivo deste estudo foi avaliar os cimentos de ionômero de vidro reforçados com resina Fuji Ortho LC e Fuji Ortho Band (GC América Corporation, Tokyo, Japan) quanto a resistência ao cisalhamento e liberação de flúor. Para avaliação da resistência ao cisalhamento utilizou-se 60 incisivos inferiores permanentes bovinos divididos em três grupos (n = 15). No Grupo 1, 2 e 3, as colagens foram realizadas com Transbond XT, Fuji Ortho LC e Fuji Ortho Band respectivamente. Após a colagem realizou-se o ensaio de cisalhamento de toda amostra à velocidade de 0,5 mm por minuto. A liberação de flúor dos materiais foram medidas durante 28 dias (1h, 24 h, 3, 7, 14, 21 e 28 dias) através de eletrodo íon seletivo conectado a um analisador de íons. Os resultados demonstraram que quanto a resistência ao cisalhamento (MPa) houve diferenças estatísticas entre os grupos 1 e 3, 2 e 3 (p > 0,05). Quanto a liberação de flúor os resultados evidenciaram diferença estatisticamente significante entre os grupos 1 e 3 e 2 e 3 em todos os tempos (p = 0.00) e entre os grupos 1 e 2 na avaliação de 3 dias de liberação de flúor (p = 0.00). Baseado nos resultados obtidos conclui-se que os materiais Transbond XT e Fuji Ortho possuem melhor resistência ao cisalhamento por??m menor liberação de flúor quando comparado ao Fuji Ortho Band.
ABSTRACT
The objective of this study was to evaluate two resin-reinforced glass ionomer cements, Fuji Ortho LC and Fuji Ortho Band (GC América Corporation, Tokyo, Japan) in terms of shear bond strength and fluoride release. Sixty bovine permanent lower incisors were divided into three groups (n = 15). In Groups 1, 2, and 3 the bonding procedures were performed with Transbond XT, Fuji Ortho LC, and Fuji Ortho Band materials respectively. Next, the samples were submitted to bond strength testing at crosshead speed of 0.5 mm/minute. Fluoride release from such materials was measured during 28 days (1h, 24 h, 3, 7, 14, 21, and 28 days) by means of selective ion electrodes connected to an ion analyser. With respect to the shear bond strength (MPa), the results demonstrated statistical differences between groups 1 and 3 as well as between groups 2 and 3. With respect to the fluoride release, the results showed statistically significant results between groups 1 and 3 as well as between groups 2 and 3 for all time periods (p = 0.00). Also, the 3-day evaluation showed statistical differences between groups 1 and 2 regarding fluoride release (p = 0.00). Based on the results obtained in the present study, one can conclude that Transbond XT and Fuji Ortho materials have a better shear bond strength than the Fuji Ortho Band one, although the latter releases less fluoride.
Texto completo:
DisponíveL
Índice:
LILACS (Américas)
Assunto principal:
Técnicas In Vitro
/
Resinas Compostas
/
Resistência ao Cisalhamento
/
Flúor
/
Cimentos de Ionômeros de Vidro
Tipo de estudo:
Estudos de avaliação
Limite:
Animais
Idioma:
Português
Revista:
Rev. odonto ciênc
Assunto da revista:
Odontologia
Ano de publicação:
2007
Tipo de documento:
Artigo
País de afiliação:
Brasil
Instituição/País de afiliação:
Universidade Federal do Rio de Janeiro/BR
Similares
MEDLINE
...
LILACS
LIS