Resistência à degradação de restaurações em dentina sadia e afetada por cárie de dentes decíduos submetidas a desafios mecânico e cariogênico / Resistance to degradation of restorations on sound and affected dentin of primary teeth submitted to mechanical and carious challenges
São Paulo; s.n; 2008. 91 p. ilus, tab, graf, CD. (BR).
Tese em Português | LILACS, BBO | ID: lil-538771
RESUMO
Este estudo objetivou investigar a resistência à degradação de restaurações de cimento de ionômero de vidro modificado por resina (CIVMR) e adesivo/resina composta sobre dentina sadia e afetada por cárie de dentes decíduos submetidas a desafio cariogênico e ciclagem mecânica, por meio de teste de microtração e nanoinfiltração. Cavidades oclusais tipo Classe I foram preparadas em 60 molares decíduos esfoliados. Metade dos dentes foi submetida ao processo de indução de cárie artificial, por meio de ciclagem de pH. Os dentes foram aleatoriamente restaurados com um dos dois materiais um CIVRM (Vitremer®) e um sistema adesivo de condicionamento total (Adper Single Bond 2®) seguido de resina composta (Filtek Z100®). Após 24 horas de armazenagem em água a 37°C, as amostras dos grupos controle seguiram para os procedimentos de teste, enquanto as demais foram re-divididas e submetidas a dois métodos de desafio desafio cariogênico (ciclagem de pH) e ciclagem mecânica (50.000 ciclos, 90 N, 3 Hz). Para os testes, os dentes foram seccionados em fatias seriadas de aproximadamente 1mm de espessura, das quais uma foi separada para o teste de nanoinfiltração e as demais foram seccionadas no sentido perpendicular de forma a obter espécimes em formato de palito com 1 mm² de área, que foram fixados a uma máquina de ensaios universal e submetidos ao teste de microtração. Os valores nominais de resistência de união foram registrados em MPa e analisados por meio de ANOVA e testes de comparações múltiplas de Games-Howel (α=0,05). As fatias designadas para o teste de nanoinfiltração foram impermeabilizadas com esmalte exceto nas interfaces e imersos em nitrato de prata amoniacal por 24 horas para evidenciação dos espaços nanométricos e sinais de degradação nas interfaces...
ABSTRACT
This study aimed to investigate the resistance to degradation of resin modified glass ionomer cement (RMGIC) and adhesive/composite restorations on sound and caries-affected dentin of primary teeth subjected to carious challenge and load-cycling, by means of microtensile test and nanoleakage. Occlusal class I cavities were prepared on sixty sound exfoliated second primary molars. Half teeth were submitted to pH-cycling to induce artificial caries lesion. Teeth were randomly restored with one of the two materials (1) a RMGIC (Vitremer®) and a (2) a total-etch adhesive system (Adper Single Bond 2®) followed by composite resin (Filtek Z100®). After storage in distilled water 37°C for 24 hours, sample from control groups followed to test procedures while the other ones were re-divided and submitted to two different aging

methods:

carious challenge (pH-cycling) and load-cycling (50 000 cycles, 90N, 3Hz). For testing, teeth were sectioned into about 1mm slabs, from which, one was separated for nanoleakage testing and the others were perpendicularly sectioned into 1mm² beams that were tested to failure in tension in a universal testing machine. Data on microtensile bond strengths were registered in MPa and analyzed by ANOVA and Games-Howell multiple-comparisons tests (α=0.05). Slabs meant for nanoleakage testing were coated with nail varnish except for the bonded interfaces, and immersed in ammoniacal AgNO3 for 24 hours in order to disclose nanometer-sized spaces and degradation signs within interfaces. After immersion in photodeveloping solution, bonded sections were prepared and observed under SEM...
Assuntos
Buscar no Google
Índice: LILACS (Américas) Assunto principal: Odontopediatria / Cárie Dentária / Restauração Dentária Permanente Tipo de estudo: Ensaio Clínico Controlado Idioma: Português Ano de publicação: 2008 Tipo de documento: Tese

Similares

MEDLINE

...
LILACS

LIS

Buscar no Google
Índice: LILACS (Américas) Assunto principal: Odontopediatria / Cárie Dentária / Restauração Dentária Permanente Tipo de estudo: Ensaio Clínico Controlado Idioma: Português Ano de publicação: 2008 Tipo de documento: Tese