Flexural strength of acrylic resin repairs processed by different methods: water bath, microwave energy and chemical polymerization
J. appl. oral sci
;
19(3): 249-253, May-June 2011. ilus, graf, tab
Artigo
em Inglês
| LILACS
| ID: lil-588131
ABSTRACT
Denture fractures are common in daily practice, causing inconvenience to the patient and to the dentists. Denture repairs should have adequate strength, dimensional stability and color match, and should be easily and quickly performed as well as relatively inexpensive. OBJECTIVE: The aim of this study was to evaluate the flexural strength of acrylic resin repairs processed by different methods: warm water-bath, microwave energy, and chemical polymerization. MATERIAL AND METHODS: Sixty rectangular specimens (31x10x2.5 mm) were made with warm water-bath acrylic resin (Lucitone 550) and grouped (15 specimens per group) according to the resin type used to make repair procedure: 1) specimens of warm water-bath resin (Lucitone 550) without repair (control group); 2) specimens of warm water-bath resin repaired with warm water-bath; 3) specimens of warm water-bath resin repaired with microwave resin (Acron MC); 4) specimens of warm water-bath resin repaired with autopolymerized acrylic resin (Simplex). Flexural strength was measured with the three-point bending in a universal testing machine (MTS 810 Material Test System) with load cell of 100 kgf under constant speed of 5 mm/min. Data were analyzed statistically by Kruskal-Wallis test (p<0.05). RESULTS: The control group showed the best result (156.04±1.82 MPa). Significant differences were found among repaired specimens and the results were decreasing as follows: group 3 (43.02±2.25 MPa), group 2 (36.21±1.20 MPa) and group 4 (6.74±0.85 MPa). CONCLUSION: All repaired specimens demonstrated lower flexural strength than the control group. Repairs with autopolymerized acrylic resin showed the lowest flexural strength.
Texto completo:
DisponíveL
Índice:
LILACS (Américas)
Assunto principal:
Resinas Acrílicas
/
Reparação em Dentadura
Idioma:
Inglês
Revista:
J. appl. oral sci
Assunto da revista:
Odontologia
Ano de publicação:
2011
Tipo de documento:
Artigo
País de afiliação:
Brasil
Instituição/País de afiliação:
São Paulo State University/BR
Similares
MEDLINE
...
LILACS
LIS