Efeito do uso de retificadores e do método de fundição em coroas unitárias implantossuportadas: análise em microscopia óptica e extensometria / Effect of rectifiers and casting methods in single-tooth implant-supported crowns: light microscopy and strain gauge analysis
Gonçalves, Marianna Cavalheiro; Nogueira Junior, Lafayette; Queiroz, José Renato Cavalcanti de.
  • Gonçalves, Marianna Cavalheiro; UNESP. FOSJC. São José dos Campos. BR
  • Nogueira Junior, Lafayette; UNESP. FOSJC. São José dos Campos. BR
  • Queiroz, José Renato Cavalcanti de; UNESP. FOSJC. São José dos Campos. BR
ImplantNews ; 7(6): 830-834, 2010. tab
Artigo em Português | LILACS, BBO | ID: lil-599216
RESUMO

Objetivo:

avaliar, in vitro, a adaptação marginal de cilindros pré-fabricados de Co-Cr e cilindros plásticos fundidos em Ni-Cr a pilares do tipo Micro-Unit por meio da microscopia ótica, variando o método de fundição e o uso ou não de retificadores. Durante o ensaio verificou-se, por meio da extensometria, a tensão gerada ao redor do implante durante o aperto do parafuso. Material e

Métodos:

36 cilindros tipo Micro-Unit foram subdivididos em três grupos (n = 12) G1 - pré-fabricados em Co-Cr (controle); G2 - fundidos em níquel-cromo (Ni-Cr) pelo método convencional; G3 - fundidos em Ni-Cr pelo método de indução. Para cada cilindro foram realizadas 32 leituras no microscópio óptico (200 x) e mensuração da tensão (extensometria) durante o aperto do parafuso de fixação, com torquímetro eletrônico. Posteriormente, os cilindros dos grupos 2 e 3 foram retificados formando dois subgrupos G2b e G3b, os quais foram novamente analisados em microscópio óptico e na extensometria.

Resultados:

os valores (μm) para desadaptação marginal (média/desvio-padrão) nos grupos foram G1- 33,3; G2a- 61,86 (16,6); G2b- 26,12 (5,5); G3a- 61,57 (22,7); G3b- 28,74 (6,9). Na extensometria (μƐ) foram G1- 162,14; G2a- 185,42 (94,8); G2b- 168,75 (122,2); G3a- 105,42 (38,5); G3b- 92,0 (33,6).

Conclusão:

a retificação dos cilindros fundidos em liga de Ni-Cr reduziu significativamente a desadaptação marginal para ambos os métodos de fundição e o uso da técnica de fundição por indução diminuiu a microdeformação ao redor do implante.
ABSTRACT

Objective:

to evaluate, in vitro by light microscopy, the marginal fit between microunit-like abutments and different types of cylinders. Also, strain gauge analysis was used to verify tension during screw tightening. Materials and

methods:

Thirty-six Microunit-like cylinders were subdivided into three groups G1 (control) - 12 prefabricated cylinders (Co-Cr); G2 - 12 plastic cylinders (conventional casting in Ni-Cr); G3 - 12 plastic cylinders (casting for induction in Ni-Cr). Light microscopic analysis provided 32 measurements around the interface. The strains gauge analysis was carried with a 10Ncm torque under electronic torque-controlling device. After, the cylinders of G2 and G3 had been rectified forming two sub-groups G2b and G3b, which again had been analyzed according to the same methods.

Results:

Mean and SD values of marginal fit (μm) were G1- 33.3; G2a- 61.86 (16.6); G2b- 26.12 (5.5); G3a- 61.57 (22.7); G3b- 28.74 (6.9). Mean μƐ (SD) values were G1- 162.14; G2a- 185.42 (94.8); G2b- 168.75 (122.2); G3a- 105.42 (38.5); G3b- 92.0 (33.6).

Conclusion:

the use of rectifiers in the Ni-Cr cast cylinders reduced the marginal fit for both casting methods and the use of the induction casting procedures diminished the μƐ values around implant.
Assuntos

Buscar no Google
Índice: LILACS (Américas) Assunto principal: Teste de Materiais / Implantes Dentários / Adaptação Marginal Dentária Idioma: Português Revista: ImplantNews Assunto da revista: Odontologia Ano de publicação: 2010 Tipo de documento: Artigo País de afiliação: Brasil Instituição/País de afiliação: UNESP/BR

Similares

MEDLINE

...
LILACS

LIS

Buscar no Google
Índice: LILACS (Américas) Assunto principal: Teste de Materiais / Implantes Dentários / Adaptação Marginal Dentária Idioma: Português Revista: ImplantNews Assunto da revista: Odontologia Ano de publicação: 2010 Tipo de documento: Artigo País de afiliação: Brasil Instituição/País de afiliação: UNESP/BR