Resistência de união ao cisalhamento de cimentos resinosos autocondicionantes à dentina / Dentin shear bond strength of two self-etch resin cements
Sander, Renata Fontanella; Prates, Luiz Henrique Maykot; Chain, Marcelo Carvalho; Clavo, Maria Cristina Marino.
Afiliação
  • Sander, Renata Fontanella; s.af
  • Prates, Luiz Henrique Maykot; Universidade Federal de Santa Catarina. Florianópolis. BR
  • Chain, Marcelo Carvalho; Universidade Federal de Santa Catarina. Florianópolis. BR
  • Clavo, Maria Cristina Marino; Universidade Federal de Santa Catarina. Departamento de Saúde Pública. Florianópolis. BR
Rev. clín. pesq. odontol. (Impr.) ; 5(3): 273-279, set.-dez. 2009. ilus, tab
Article em Pt | LILACS, BBO | ID: lil-617427
Biblioteca responsável: BR28.1
RESUMO

OBJETIVO:

Avaliar a resistência de união à dentina de dois cimentos resinosos autocondicionantes RelyX UnicemTM, 3M ESPETM (G1) e MaxcemTM – Kerr (G2), e de um cimento resinoso convencional RelyX ARC – 3M ESPETM (G3), por meio de teste cisalhamento. MATERIAL E

MÉTODO:

Vinte e três molares humanos, hígidos e recém-extraídos, foram seccionados no limite amelocementário e no sentido mésio-distal, aproveitando-se as superfícies vestibulares e linguais das coroas. Os fragmentos foram embutidos com resina acrílica em tubos de PVC, de modo que as faces vestibulares e linguais ficassem expostas. Utilizaram-se lixas de carbeto de silício, sob refrigeração, para a obtenção de superfícies planas de dentina. Após a delimitação das áreas destinadas à cimentação, a amostra foi distribuída em três grupos de 15 espécimes cada. Uma matriz de teflon bipartida permitiu a confecção de cilindros dos cimentos coincidentes com as áreas delimitadas. Os testes de resistência de união, sob cisalhamento, foram realizados em máquina Instron 4444 (0,5 mm/min.), após 24 horas de armazenagem em água a 37oC. Os dados foram analisados por ANOVA e teste de Tukey (5%).

RESULTADOS:

Os valores médios para cada grupo foram (MPa) G17,15 (2,74); G24,15 (1,87); G39,69 (3,02); foram observadas diferenças estatisticamente significativas entre os três grupos avaliados.

CONCLUSÕES:

Os resultados demonstraram superioridade do cimento resinoso convencional sobre os autocondicionantes; estes também apresentaram diferenças entre si.
ABSTRACT

OBJECTIVE:

To evaluate the dentin shear bond strength of two self-etch resin cements RelyX Unicem-3M ESPETM (G1) e Maxcem-KerrTM (G2) and a conventional cement RelyX ARC-3M ESPETM (G3). MATERIAL AND

METHOD:

Twenty-three freshly extracted noncarious human molars were cut at the dentin enamel junction and posteriorly mesiodistally in order to use lingual and buccal surfaces of the crowns. The fragments were embedded in PVC tubes with acrylic resin exposing the buccal and lingual surfaces, which were grinded under refrigeration on silicon carbide papers to obtain a flat and smooth dentin surface. After demarcation of cementation’s areas, the specimens were distributed into three groups (n=15). A special split Teflon mold allowed manufacturing of cement cylinders, which match the demarcated areas. The shear bond strength test was performed in an 4444 Instron machine (0.5 mm / min.), after 24 hours of storage in water at 37°C. RESULTS AND

CONCLUSION:

The data were analyzed by ANOVA and Tukey’s Test (5%). The means (MPa) were G1 7.15 (2.74); G2 4.15 (1.87) and G3 9.69 (3.02), with significant differences among the three groups evaluated. The conventional resin cement has shown superior adhesion property over the self etching cement, which presented statistical differences between them.
Assuntos
Palavras-chave
Texto completo: 1 Índice: LILACS Assunto principal: Técnicas In Vitro / Cimentos de Resina / Dentina Limite: Humans Idioma: Pt Revista: Rev. clín. pesq. odontol. (Impr.) Assunto da revista: ODONTOLOGIA Ano de publicação: 2009 Tipo de documento: Article
Texto completo: 1 Índice: LILACS Assunto principal: Técnicas In Vitro / Cimentos de Resina / Dentina Limite: Humans Idioma: Pt Revista: Rev. clín. pesq. odontol. (Impr.) Assunto da revista: ODONTOLOGIA Ano de publicação: 2009 Tipo de documento: Article