Efeito da desinfecção associada à escovação na rugosidade superficial de resina acrílica termopolimerizável / Effect of disinfection associated to brushing on surface roughness of heat-polymerized acrylic resin
Figueiredo, Mariana Diehl; Nogueira Junior, Lafayette; Queiroz, José Renato Cavalcanti de; Pavanelli, Carlos Augusto.
  • Figueiredo, Mariana Diehl; Universidade Estadual Paulista. FOSJC. São José dos Campos. BR
  • Nogueira Junior, Lafayette; Universidade Estadual Paulista. FOSJC. São José dos Campos. BR
  • Queiroz, José Renato Cavalcanti de; Universidade Estadual Paulista. FOSJC. São José dos Campos. BR
  • Pavanelli, Carlos Augusto; Universidade Estadual Paulista. FOSJC. São José dos Campos. BR
Braz. dent. sci ; 14(1/2): 49-53, 2011. tab
Artigo em Português | LILACS, BBO | ID: lil-642712
RESUMO
O objetivo desse estudo é avaliar o efeito da desinfecção associada à escovação na rugosidade (Ra e Rz) superficial de resina acrílica termopolimerizável. Cinquenta cilindros de resina acrílica (Lucitone 550 Dentsply) de dimensões 0,5 mm x 0,5 mm foram confeccionados, utilizando-se o ciclo térmico curto de polimerização (73°C por 90 min, seguidos por imersão em água a 94°C durante 30 min), de acordo com as instruções do fabricante. Os espécimes termopolimerizados foram imersos em água destilada a 37 ±1°C por 48 horas e divididos em 5 grupos (n=10) de acordo com o método de desinfecção GrControle- sem desinfecção e sem escovação; Gr1-água destilada seguido de escovação; Gr2- hipoclorito de Sódio 1% seguido de escovação; Gr3- gluconato de clorexidina 2% seguido de escovação, e G4- perborato de sódio a 3,78% seguido de escovação. Os grupos foram imersos por 5 min nas soluções correspondentes antes do ciclo de escovação (10.000 ciclos). Foram analisados em rugosímetro de contato os valores para Ra e Rz. Os resultados foram analisados estatisticamente pelo método ANOVA e as médias comparadas pelo teste de Tukey (α=0,05). As médias obtidas para o Ra e Rz respectivamente foram Gr controle 0,16 (0,03) e 0,77 (0,21); Gr1 0,3 (0,13) e 1,25 (0,62); Gr2 0,24(0,09) e 1,02 (0,4); Gr3 0,34 (0,14) e 1,45(0,55); Gr4 0,38(0,14) e 1,7(0,65). O teste ANOVA revelou que a rugosidade para os dois parâmetros foi significativamente afetada pela abrasão provocada pela escovação com dentifrício (PRa=0,0009; PRz=0,0021). Pode-se concluir que a escovação associada à desinfecção com hipoclorito de sódio produziu menor efeito sobre a rugosidade da superfície da resina acrílica que os demais desinfetantes testados.
ABSTRACT
The aim of this study was to evaluate the effect of disinfection associated to brushing the superficial crease (Ra and Rz) of heat-polymerized acrylic resin. Fifty cylinders of 0.5mm x o.5mm acrylic resin (Lucitone 550 Dentsply) were produced by using the short thermal cycle of polymerization (73ºC for 90 minutes and then immersion on water at the temperature of 94ºC for 30 minutes), according to the manufacturer’s instructions. The thermo-polymerized samples were immersed in distilled water at the temperature of 37ºC (plus or minus 1ºC) for 48 hours and divided into 5 groups (n=10) according to the disinfection method, that is GrControl – no chemical disinfection nor brushing; Gr1 – distilled water and brushing; Gr2 – sodium hypoclorite 1% and brushing; Gr3 – chlorexidine gluconate 2% and brushing and G4 – sodium perborate 3,78% and brushing. The groups were immersed for 5 minutes before brushing cycle (10.000 cycles) and the values for Ra and Rz were analyzed with crease contact measuring instrument(contact profilometer). Results were statistically analyzed by the ANOVA method. The arithmetic means were compared by the Tukey test (ά=0.05).

RESULTS:

The arithmetic means obtained for Ra and Rz were GrControl 0.16(0.03) and 0.77 (0.21); Gr1 0.3(0.13) and 1.25(0.62); Gr2 0.24(0.09) and 1.02(0.4); Gr3 0.34(0.14) and 1.45(0.55); Gr4 0.38(0.14) and 1.7(0.65) . The ANOVA test revealed that the roughness for the two parameters was significantly affected by brushing with toothpaste (PRa =0.0009; PRz=0.0021) .Tooth brushing together with sodium hypoclorite results in a lessened effect over the surface crease of the acrylic resin than other tested disinfectants
Assuntos

Texto completo: DisponíveL Índice: LILACS (Américas) Assunto principal: Resinas Acrílicas / Desinfecção Tipo de estudo: Fatores de risco Idioma: Português Revista: Braz. dent. sci Assunto da revista: Odontologia / Sa£de Bucal Ano de publicação: 2011 Tipo de documento: Artigo País de afiliação: Brasil Instituição/País de afiliação: Universidade Estadual Paulista/BR

Similares

MEDLINE

...
LILACS

LIS

Texto completo: DisponíveL Índice: LILACS (Américas) Assunto principal: Resinas Acrílicas / Desinfecção Tipo de estudo: Fatores de risco Idioma: Português Revista: Braz. dent. sci Assunto da revista: Odontologia / Sa£de Bucal Ano de publicação: 2011 Tipo de documento: Artigo País de afiliação: Brasil Instituição/País de afiliação: Universidade Estadual Paulista/BR