Analysis of the color alteration and radiopacity promoted by bismuth oxide in calcium silicate cement
Braz. oral res
;
27(4): 318-323, Jul-Aug/2013. tab, graf
Artigo
em Inglês
| LILACS
| ID: lil-679218
ABSTRACT
The aim of the study was to determine if the increase in radiopacity provided by bismuth oxide is related to the color alteration of calcium silicate-based cement. Calcium silicate cement (CSC) was mixed with 0%, 15%, 20%, 30% and 50% of bismuth oxide (BO), determined by weight. Mineral trioxide aggregate (MTA) was the control group. The radiopacity test was performed according to ISO 6876/2001. The color was evaluated using the CIE system. The assessments were performed after 24 hours, 7 and 30 days of setting time, using a spectrophotometer to obtain the ΔE, Δa, Δb and ΔL values. The statistical analyses were performed using the Kruskal-Wallis/Dunn and ANOVA/Tukey tests (p < 0.05). The cements in which bismuth oxide was added showed radiopacity corresponding to the ISO recommendations ( > 3 mm equivalent of Al). The MTA group was statistically similar to the CSC / 30% BO group (p > 0.05). In regard to color, the increase of bismuth oxide resulted in a decrease in the ΔE value of the calcium silicate cement. The CSC group presented statistically higher ΔE values than the CSC / 50% BO group (p < 0.05). The comparison between 24 hours and 7 days showed higher ΔE for the MTA group, with statistical differences for the CSC / 15% BO and CSC / 50% BO groups (p < 0.05). After 30 days, CSC showed statistically higher ΔE values than CSC / 30% BO and CSC / 50% BO (p < 0.05). In conclusion, the increase in radiopacity provided by bismuth oxide has no relation to the color alteration of calcium silicate-based cements.
Texto completo:
DisponíveL
Índice:
LILACS (Américas)
Assunto principal:
Materiais Restauradores do Canal Radicular
/
Bismuto
/
Silicatos
/
Pigmentação em Prótese
/
Compostos de Cálcio
/
Cimentos Dentários
Limite:
Humanos
Idioma:
Inglês
Revista:
Braz. oral res
Assunto da revista:
Odontologia
Ano de publicação:
2013
Tipo de documento:
Artigo
/
Documento de projeto
País de afiliação:
Brasil
Instituição/País de afiliação:
Universidade de Sao Paulo/BR
Similares
MEDLINE
...
LILACS
LIS