Stress distribution on dentin-cement-post interface varying root canal and glass fiber post diameters. A three-dimensional finite element analysis based on micro-CT data
J. appl. oral sci
;
21(6): 511-517, Nov-Dec/2013. tab, graf
Artigo
em Inglês
| LILACS, BBO
| ID: lil-697821
ABSTRACT
Objective: The aim of the present study was to analyze the influence of root canal and glass fiber post diameters on the biomechanical behavior of the dentin/cement/post interface of a root-filled tooth using 3D finite element analysis. Material and Methods: Six models were built using micro-CT imaging data and SolidWorks 2007 software, varying the root canal (C) and the glass fiber post (P) diameters: C1P1-C=1 mm and P=1 mm; C2P1-C=2 mm and P=1 mm; C2P2-C=2 mm and P=2 mm; C3P1-C=3 mm and P=1 mm; C3P2-C=3 mm and P=2 mm; and C3P3-C=3 mm and P=3 mm. The numerical analysis was conducted with ANSYS Workbench 10.0. An oblique force (180 N at 45º) was applied to the palatal surface of the central incisor. The periodontal ligament surface was constrained on the three axes (x=y=z=0). Maximum principal stress (σmax) values were evaluated for the root dentin, cement layer, and glass fiber post. Results: The most evident stress was observed in the glass fiber post at C3P1 (323 MPa), and the maximum stress in the cement layer occurred at C1P1 (43.2 MPa). The stress on the root dentin was almost constant in all models with a peak in tension at C2P1 (64.5 MPa). CONCLUSION: The greatest discrepancy between root canal and post diameters is favorable for stress concentration at the post surface. The dentin remaining after the various root canal preparations did not increase the stress levels on the root. .
Texto completo:
DisponíveL
Índice:
LILACS (Américas)
Assunto principal:
Técnica para Retentor Intrarradicular
/
Cimentos Dentários
/
Cavidade Pulpar
/
Dentina
/
Vidro
Tipo de estudo:
Estudos de avaliação
Limite:
Humanos
Idioma:
Inglês
Revista:
J. appl. oral sci
Assunto da revista:
Odontologia
Ano de publicação:
2013
Tipo de documento:
Artigo
País de afiliação:
Brasil
Instituição/País de afiliação:
Univ. Estadual Paulista/BR
Similares
MEDLINE
...
LILACS
LIS