Bonding performance of a self-adhering flowable composite to indirect restorative materials
RSBO (Impr.)
;
11(1): 6-13, Jan.-Mar. 2014. tab
Artigo
em Inglês
| LILACS
| ID: lil-718000
ABSTRACT
Introduction:
Simplified restorative materials may be a logical next step for dental manufacturers.Objective:
The aim of this study was to evaluate the shear bond strength of a self-adhering flowable composite to four substrates used in indirect technique. Material andmethods:
Twenty-four samples (5 mm wide, 15 mm length and 2 mm thick / six blocks each substrate) were prepared in the dental prosthetic laboratory. The following materials were used ceromer (SR Adoro/AD, Ivoclar Vivadent), leucite ceramic (IPS Empress Esthetic/EE, Ivoclar Vivadent), zirconia ceramic (ZirCAD/ZI, Ivoclar Vivadent); metal ceramic alloy (Fit Cast SB/ME, Talladium do Brasil). Samples of each substrate were divided into two groups (n = 3). Two flowable composites (Control/FF - Filtek Z350 XT Flow/3M ESPE, and the self-adhering/DF - Dyad Flow/Kerr) were bonded to the four substrates. Four Tygon tubings were positioned over each sample, which were filled in with the composites FF and DF, and visible light-cured for 20 s. The tubings were removed to expose the specimens (12 per group) in format of cylinders and samples were stored in distilled water at 37±2°C for one week. After this period, each sample was attached to testing machine and the specimens were submitted to the shear bond strength test at speed of 1.0 mm/min, until failure. The results were analyzed by two-way ANOVA and Tukey test (p < 0.05).Results:
The means (SD) were (in MPa) AD + FF = 34.4 ± 4.9; AD + DF = 28.2 ± 4.2; EE + FF = 29.7 ± 5.8; EE + DF = 32.3 ± 6.9; ZI + FF = 23.2 ± 5.4; ZI + DF = 8.5 ± 1.5; ME + FF = 28.9 ± 4.2; ME + DF = 31.7 ± 4.5.Conclusion:
The efficacy of flowable composites is material-dependent. The self-adhering composite provided lower bond strength only to zirconia ceramic. Comparing with the control group, Dyad Flow showed lower bond strength to the ceromer and zirconia ceramic.
Texto completo:
DisponíveL
Índice:
LILACS (Américas)
Idioma:
Inglês
Revista:
RSBO (Impr.)
Assunto da revista:
Odontologia
Ano de publicação:
2014
Tipo de documento:
Artigo
País de afiliação:
Brasil
Instituição/País de afiliação:
University of Itajai Valley/BR
Similares
MEDLINE
...
LILACS
LIS