The effect of the strength and wetting characteristics of Bis-GMA/TEGDMA-based adhesives on the bond strength to dentin / 대한치과보존학회지
Journal of Korean Academy of Conservative Dentistry ; : 139-148, 2011.
Artigo em Inglês | WPRIM | ID: wpr-178057
ABSTRACT

OBJECTIVES:

This study investigated the effect of the strength and wetting characteristics of adhesives on the bond strength to dentin. The experimental adhesives containing various ratios of hydrophobic, low-viscosity Bis-M-GMA, with Bis-GMA and TEGDMA, were made and evaluated on the mechanical properties and bond strength to dentin. MATERIALS AND

METHODS:

Five experimental adhesives formulated with various Bis-GMA/Bis-M-GMA/TEGDMA ratios were evaluated on their viscosity, degree of conversion (DC), flexural strength (FS), and microtensile bond strength (MTBS). The bonded interfaces were evaluated with SEM and the solubility parameter was calculated to understand the wetting characteristics of the adhesives.

RESULTS:

Although there were no significant differences in the DC between the experimental adhesives at 48 hr after curing (p > 0.05), the experimental adhesives that did not contain Bis-GMA exhibited a lower FS than did those containing Bis-GMA (p < 0.05). The experimental adhesives that had very little to no TEGDMA showed significantly lower MTBS than did those containing a higher content of TEGDMA (p < 0.05). The formers exhibited gaps at the interface between the adhesive layer and the hybrid layer. The solubility parameter of TEGDMA approximated those of the components of the primed dentin, rather than Bis-GMA and Bis-M-GMA.

CONCLUSIONS:

To achieve a good dentin bond, a strong base monomer, such as Bis-GMA, cannot be completely replaced by Bis-M-GMA for maintaining mechanical strength. For compatible copolymerization between the adhesive and the primed dentin as well as dense cross-linking of the adhesive layer, at least 30% fraction of TEGDMA is also needed.
Assuntos

Texto completo: DisponíveL Índice: WPRIM (Pacífico Ocidental) Assunto principal: Polietilenoglicóis / Ácidos Polimetacrílicos / Solubilidade / Viscosidade / Compostos Benzidrílicos / Quimera / Adesivos / Bis-Fenol A-Glicidil Metacrilato / Dentina / Metacrilatos Idioma: Inglês Revista: Journal of Korean Academy of Conservative Dentistry Ano de publicação: 2011 Tipo de documento: Artigo

Similares

MEDLINE

...
LILACS

LIS

Texto completo: DisponíveL Índice: WPRIM (Pacífico Ocidental) Assunto principal: Polietilenoglicóis / Ácidos Polimetacrílicos / Solubilidade / Viscosidade / Compostos Benzidrílicos / Quimera / Adesivos / Bis-Fenol A-Glicidil Metacrilato / Dentina / Metacrilatos Idioma: Inglês Revista: Journal of Korean Academy of Conservative Dentistry Ano de publicação: 2011 Tipo de documento: Artigo