In vitro study of fracture strength of provisional crown materials
The Journal of Advanced Prosthodontics ; : 27-31, 2015.
Artigo em Inglês | WPRIM | ID: wpr-220557
ABSTRACT

PURPOSE:

The purpose of this report was to evaluate the effect of the fabrication method and material type on the fracture strength of provisional crowns. MATERIALS AND

METHODS:

A master model with one crown (maxillary left second premolar) was manufactured from Cr-Co alloy. The master model was scanned, and the data set was transferred to a CAD/CAM unit (Yenamak D50, Yenadent Ltd, Istanbul, Turkey) for the Cercon Base group. For the other groups, temporary crowns were produced by direct fabrication methods (Imident, Temdent, Structur Premium, Takilon, Systemp c&b II, and Acrytemp). The specimens were subjected to water storage at 37degrees C for 24 hours, and then they were thermocycled (TC, 5000x, 5-55degrees C) (n=10). The maximum force at fracture (Fmax) was measured in a universal test machine at 1 mm/min. Data was analyzed by non-parametric statistics (alpha=.05).

RESULTS:

Fmax values varied between 711.09-1392.1 N. In the PMMA groups, Takilon showed the lowest values (711.09 N), and Cercon Base showed the highest values (959.59 N). In the composite groups, Structur Premium showed the highest values (1392.1 N), and Acrytemp showed the lowest values (910.05 N). The composite groups showed significantly higher values than the PMMA groups (P=.01).

CONCLUSION:

Composite-based materials showed significantly higher fracture strengths than PMMA-based materials. The CAD-CAM technique offers more advantages than the direct technique.
Assuntos

Texto completo: DisponíveL Índice: WPRIM (Pacífico Ocidental) Assunto principal: Água / Desenho Assistido por Computador / Polimetil Metacrilato / Coroas / Ligas / Conjunto de Dados Idioma: Inglês Revista: The Journal of Advanced Prosthodontics Ano de publicação: 2015 Tipo de documento: Artigo

Similares

MEDLINE

...
LILACS

LIS

Texto completo: DisponíveL Índice: WPRIM (Pacífico Ocidental) Assunto principal: Água / Desenho Assistido por Computador / Polimetil Metacrilato / Coroas / Ligas / Conjunto de Dados Idioma: Inglês Revista: The Journal of Advanced Prosthodontics Ano de publicação: 2015 Tipo de documento: Artigo