Preparation of hydroxyapatite-containing titania film on the surface of pure titanium by micro-arc oxidation technique / 生物医学工程学杂志
Journal of Biomedical Engineering
;
(6): 127-130, 2008.
Artigo
em Chinês
| WPRIM
| ID: wpr-230640
ABSTRACT
A porous hydroxylapatite-containing titania film was prepared by an electrochemical oxidation method, i.e. micro-arc oxidation (MAO). During the oxidation treatment, the titanium sample was immersed in electrolytic solution containing calcium acetate monohydrate and sodium biphosphate dihydrate by using a pulse power supply. The thickness, phase, composition and morphology of the oxide coating were monitored with X-ray diffraction (XRD) and scanning electron microscopy (SEM) with energy dispersive X-ray spectrometer (EDS). The thickness of the MAO film is about 20 microm and the coating where each porous size is no more than 5 microm was porous and uneven, without apparent interface to the titanium substrates. The coating formed in the Ca- and P-containing solution with MAO contained Ca and P along with Ti and O. The Ca/P ratio on the surface is 1.63, while that in the interface is 0.51. XRD showed that the porous coating was made up of anatase, rutile and hydroxyapatite. Such MAO films are expected to have significant medical applications as dental implants and artificial bone joints.
Texto completo:
DisponíveL
Índice:
WPRIM (Pacífico Ocidental)
Assunto principal:
Oxirredução
/
Tamanho da Partícula
/
Propriedades de Superfície
/
Titânio
/
Química
/
Porosidade
/
Durapatita
/
Materiais Revestidos Biocompatíveis
Limite:
Humanos
Idioma:
Chinês
Revista:
Journal of Biomedical Engineering
Ano de publicação:
2008
Tipo de documento:
Artigo
Similares
MEDLINE
...
LILACS
LIS