Cr-Ti-Al-N complex coating on titanium to strengthen Ti/porcelain bonding / 南方医科大学学报
Journal of Southern Medical University
; (12): 154-157, 2006.
Article
em Zh
| WPRIM
| ID: wpr-234173
Biblioteca responsável:
WPRO
ABSTRACT
<p><b>OBJECTIVE</b>To study the feasibility of magnetron sputtering Cr-Ti-Al-N complex coating as an interlayer on titanium to enhance the titanium-ceramic binding strength.</p><p><b>METHODS</b>With a three-point bending test according to ISO 9693, the binding strength of Duceratin (Degussa) to titanium substrate prepared with 4 different surface treatments (polishing, polishing and megnetron sputtering Cr, Ti, Al, and N complex coating, sandblasting, sandblasting and coating) was evaluated. Ti/porcelain interface and fractured Ti surface were examined using scanning electron microscopy with energy-dispersive spectrometry (EDS).</p><p><b>RESULTS</b>The binding strength of polished and coated titanium/Duceratin was significantly higher than polished titanium group (P<0.05). The binding strength of sandblasted and coated titanium/Duceratin did not differ significantly from that of sandblasted titanium group (P>0.05), and the strength in the two sandblasted titanium groups was significantly higher than that in polished and coated titanium group (P<0.05).</p><p><b>CONCLUSION</b>Megnetron sputtering Cr-Ti-Al-N complex on polished titanium can increase the titanium/porcelain binding strength. Megnetron sputtering coating is a promising Ti/porcelain interlayer.</p>
Texto completo:
1
Índice:
WPRIM
Assunto principal:
Padrões de Referência
/
Propriedades de Superfície
/
Resistência à Tração
/
Titânio
/
Cerâmica
/
Química
/
Cromo
/
Colagem Dentária
/
Ligas Metalo-Cerâmicas
/
Materiais Revestidos Biocompatíveis
Idioma:
Zh
Revista:
Journal of Southern Medical University
Ano de publicação:
2006
Tipo de documento:
Article