A study on the mechanical properties and microstructure of Alumina-zirconia nano-composite infiltrated ceramic / 华西口腔医学杂志
West China Journal of Stomatology
;
(6): 238-240, 2003.
Artigo
em Chinês
| WPRIM
| ID: wpr-283611
ABSTRACT
<p><b>OBJECTIVE</b>To evaluate the mechanical properties and microstructure of a new dental full-ceramic material:
alumina-zirconia nano-composite infiltrated ceramic.</p><p><b>METHODS</b>The flexural strength was tested with three-point bending method and the fracture toughness with single edge notch bend (SENB) method. The composition of crystal phases in the infiltrated ceramic was analyzed by X-ray diffraction (XRD). The microstructure of the infiltrated ceramic was examined by scanning electronic microscope (SEM).</p><p><b>RESULTS</b>The average three-point flexural strength of the material was (610.85 +/- 37.07) MPa and the average fracture toughness determined by SENB method was (6.51 +/- 1.38) MPa.m1/2. The main crystal phases in this composite ceramic were alpha-Al2O3 and TZP-ZrO2.</p><p><b>CONCLUSION</b>Alumina-zirconia nano-composite infiltrated ceramic is a new infiltrated ceramic with favorable mechanical properties. It demonstrated a promising future for clinical application.</p>
Texto completo:
DisponíveL
Índice:
WPRIM (Pacífico Ocidental)
Assunto principal:
Estresse Mecânico
/
Zircônio
/
Teste de Materiais
/
Microscopia Eletrônica de Varredura
/
Química
/
Porosidade
/
Ligas Metalo-Cerâmicas
/
Nanotecnologia
/
Materiais Dentários
/
Porcelana Dentária
Idioma:
Chinês
Revista:
West China Journal of Stomatology
Ano de publicação:
2003
Tipo de documento:
Artigo
Similares
MEDLINE
...
LILACS
LIS