Low-temperature crystallization on porous titanium and in vivo evaluation on bone-bonding mechanics of the treated titanium / 中国医疗器械杂志
Chinese Journal of Medical Instrumentation
;
(6): 245-247, 2007.
Artigo
em Chinês
| WPRIM
| ID: wpr-323276
ABSTRACT
By the bioactivity technology of Low-Temperature Preparation of Anatase and Rutile Layers on porous Titanium Substrates, CPTi(Commercially pure titanium Phi4.0 mm x 20 mm) was processed and treated as experiment specimens while CPTi was treated as control specimens. Experiment specimens and control specimens were implanted into the holes (4.0 mm in diameter) in rabbit's right and left tibias respectively. After implantation for predetermined periods of 4,8,12, 16 weeks, the specimens were taken out with bone tissues, and were examined by a press-out tester to evaluate the shearing force between the implant and the bone tissue. It is found that the shearing force between the experiment specimen and the bone is more significantly higher than that between the control specimen and the bone, and the bonding time is shorter, the stabilization time is faster. This study has laid down a good foundation for the titanium metal's innovative applications in clinical orthopaedics.
Texto completo:
DisponíveL
Índice:
WPRIM (Pacífico Ocidental)
Assunto principal:
Dispositivos de Fixação Ortopédica
/
Próteses e Implantes
/
Tíbia
/
Titânio
/
Osso e Ossos
/
Teste de Materiais
/
Química
/
Temperatura Baixa
/
Substitutos Ósseos
/
Cristalização
Limite:
Animais
Idioma:
Chinês
Revista:
Chinese Journal of Medical Instrumentation
Ano de publicação:
2007
Tipo de documento:
Artigo
Similares
MEDLINE
...
LILACS
LIS