Effect of location of glass fiber pre-impregnated with light-curing resin on the fracture strength and fracture modes of a maxillary complete denture / 대한치과보철학회지
The Journal of Korean Academy of Prosthodontics
;
: 279-284, 2012.
Artigo
em Coreano
| WPRIM
| ID: wpr-33059
ABSTRACT
PURPOSE:
This study evaluated the effect of glass fiber pre-impregnated with light-curing resin on the fracture strength and fracture modes of a maxillary complete denture. MATERIALS ANDMETHODS:
Maxillary acrylic resin complete dentures reinforced with glass fiber pre-impregnated with light-curing resin (SES MESH, INNO Dental Co., Yeoncheon-gun, Korea) and without reinforcement were tested. The reinforcing material was embedded in the denture base resin and placed different regions (Control, without reinforcement; Group A, center of anterior ridge; Group B, rugae area; Group C, center of palate; Group D, full coverage of denture base). The fracture strength and fracture modes of a maxillary complete denture were tested using Instron test machine (Instron Co., Canton, MA, USA) at a 5.0 mm/min crosshead speed. The flexure load was applied to center of denture with a 20 mm diameter ball attachment. When fracture occurred, the fracture mode was classified based on fracture lines. The data were analyzed with one-way ANOVA at the significance level of 0.05.RESULTS:
There were non-significant differences (P>.05) in the fracture strength among test groups. Group A showed anteroposterior fracture and posterior fracture mainly, group B, C and control group showed partial fracture on center area mostly. Most specimen of group D showed posterior fracture.CONCLUSION:
The location and presence of the fiber reinforcement did not affect the fracture strength of maxillary complete denture. However, reinforcing acrylic resin denture with glass fiber has a tendency to suppress the crack.
Texto completo:
DisponíveL
Índice:
WPRIM (Pacífico Ocidental)
Assunto principal:
Reforço Psicológico
/
Dentaduras
/
Bases de Dentadura
/
Prótese Total
/
Vidro
Idioma:
Coreano
Revista:
The Journal of Korean Academy of Prosthodontics
Ano de publicação:
2012
Tipo de documento:
Artigo
Similares
MEDLINE
...
LILACS
LIS