Effect of moulding and extruding conditions on mechanical properties of poly(D,L-lactide) and MDI chain-extending poly(D,L-lactide)/hydroxyapatite composite / 生物医学工程学杂志
Journal of Biomedical Engineering ; (6): 624-627, 2002.
Artigo em Chinês | WPRIM | ID: wpr-340951
ABSTRACT
In this paper, poly(D,L-lactide) (PDLLA), MDI chain-extending poly(D,L-lactide) (PDLLA/MDI) and MDI chain-extending poly(D,L-lactide)/hydroxyapatite composite (PDLLA/HA/MDI) were prepared respectively and the effects of moulding and extruding conditions on their mechanical properties were also investigated. At the optimal conditions, bending strength of PDLLA and PDLLA/MDI is 35.1 MPa and 51.3 MPa, respectively, and their bending modulus is 2413.6 MPa and 1830.9 MPa, respectively. Bending strength of PDLLA/HA and PDLLA/HA/MDI is 31.2 MPa and 55.4 MPa, respectively, and their bending modulus is 1735.0 MPa and 2068.5 MPa, respectively. These results have shown that the mechanical properties of PDLLA/MDI and PDLLA/HA/MDI have enhanced significantly by MDI chain-extending.
Assuntos
Texto completo: DisponíveL Índice: WPRIM (Pacífico Ocidental) Assunto principal: Poliésteres / Materiais Biocompatíveis / Química / Ciência de Laboratório Médico / Durapatita / Mecânica / Métodos Idioma: Chinês Revista: Journal of Biomedical Engineering Ano de publicação: 2002 Tipo de documento: Artigo

Similares

MEDLINE

...
LILACS

LIS

Texto completo: DisponíveL Índice: WPRIM (Pacífico Ocidental) Assunto principal: Poliésteres / Materiais Biocompatíveis / Química / Ciência de Laboratório Médico / Durapatita / Mecânica / Métodos Idioma: Chinês Revista: Journal of Biomedical Engineering Ano de publicação: 2002 Tipo de documento: Artigo