Effects of magnetron sputtered ZrN on the bonding strength of titanium porcelain / 中华口腔医学杂志
Chinese Journal of Stomatology
;
(12): 236-239, 2009.
Artigo
em Chinês
| WPRIM
| ID: wpr-346726
ABSTRACT
<p><b>OBJECTIVE</b>To investigate the effect of magnetron sputtered ZrN on the bonding strength between a low-fusing porcelain (Ti/Vita titankeramik system) and commercially pure cast titanium.</p><p><b>METHODS</b>Sixteen specimens were randomly assigned to test group and control group (n=8). The control group received no surface treated. Magnetron sputtered ZrN film was deposited on the surface of specimens in the test group. Then the sixteen titanium-porcelain specimens were prepared in a rectangular shape and went through three-point bending test on a universal test machine. The bond strength of Ti/porcelain was recorded. The phase composition of the specimens was analyzed using X-ray diffraction (XRD). The interface at titanium and porcelain and the titanium surface after debonding were observed with a scanning electron microscopy (SEM) and analyzed using energy depressive spectrum (EDS).</p><p><b>RESULTS</b>New phase of ZrN was found with XRD in the test group. Statistical analysis showed higher bond strength following ZrN surface treatment in the test group [(45.991+/-0.648) MPa] than that in the control group [(29.483+/-1.007) MPa] (P=0.000). Bonded ceramic could be observed in test group, the amount of bonded ceramic was more than that in the control group. No obvious bonded ceramic in control group was found.</p><p><b>CONCLUSIONS</b>Magnetron sputtered ZrN can improve bond strength of Ti/Vita titankeramik system significantly.</p>
Texto completo:
DisponíveL
Índice:
WPRIM (Pacífico Ocidental)
Assunto principal:
Propriedades de Superfície
/
Titânio
/
Zircônio
/
Teste de Materiais
/
Química
/
Porcelana Dentária
/
Análise do Estresse Dentário
Idioma:
Chinês
Revista:
Chinese Journal of Stomatology
Ano de publicação:
2009
Tipo de documento:
Artigo
Similares
MEDLINE
...
LILACS
LIS