Experimental study on bond strength of machinable composite resin and dentin with three kinds of resin cements / 中华口腔医学杂志
Chinese Journal of Stomatology
;
(12): 46-49, 2009.
Artigo
em Chinês
| WPRIM
| ID: wpr-346775
ABSTRACT
<p><b>OBJECTIVE</b>To examine the shear and microtensile bond strength between a newly developed dental machinable composite resin (polymethylmetacrylate/nano SiO2-ZrO2, PNSZ) and dentin cemented using three resin luting systems and to select the most suitable one.</p><p><b>METHODS</b>The shear and microtensile bond strength between the machinable composite resin and dentin cemented using three resin luting systems (Group ARelyX ARC, Group BPanavia-F,Group CVariolink II) were tested. The broken specimens were observed with a stereomicroscope (x 50) to compare their failure modes. RESULTS; In the shear tests, no significant difference was found in bond strength among Group A [ (14. 07 +/- 4. 67) MPa] ,Group B[ (13.17 +/- 4. 63) MPa] and Group C [ ( 12. 10 +/- 2.18) MPa] (P > 0.05) . In the microtensile tests, no significant difference was found in bond strength among Group A [(11.49 +/- 4.90) MPa],Group B[(9.66 +/- 4.15) MPa].and Group C[(10.11 +/- 4.20) MPa](P > 0. 05).The failure modes of all the three resin cements were predominantly adhesive failures at the dentin/cement interface.</p><p><b>CONCLUSIONS</b>The three types of resin cements showed similar results in bond strength between the dental machinable composite resin and dentin. Bonding at the resin/cement interface was stronger than that at the dentin/cement interface.</p>
Texto completo:
DisponíveL
Índice:
WPRIM (Pacífico Ocidental)
Assunto principal:
Poliuretanos
/
Resinas Acrílicas
/
Colagem Dentária
/
Resinas Compostas
/
Cimentos de Resina
/
Resistência ao Cisalhamento
/
Porcelana Dentária
/
Análise do Estresse Dentário
/
Dentina
Limite:
Humanos
Idioma:
Chinês
Revista:
Chinese Journal of Stomatology
Ano de publicação:
2009
Tipo de documento:
Artigo
Similares
MEDLINE
...
LILACS
LIS