Cobalt-chromium alloy with zirconium nitride coating influences adhesion properties of bacteria / 中国组织工程研究
Chinese Journal of Tissue Engineering Research ; (53): 4033-4037, 2015.
Artigo em Chinês | WPRIM | ID: wpr-461896
ABSTRACT

BACKGROUND:

Bacterial adhesion is closely related to the surface properties of cobalt-chromium al oys, and therefore, the surface modification technology has become the focus of research in this area.

OBJECTIVE:

To verify whether the cobalt-chromium al oy with zirconium nitride coating can improve the bacterial adhesion of metal denture materials.

METHODS:

Magnetron sputtering deposition method was used to plate zirconium nitride film on the surface of cobalt-chromium al oys (experimental group), and cobalt-chromium al oy specimens uncoated served as control group. Streptococcus mutans, Candida albicans, and Actinomyces viscosus were respectively inoculated on the two kinds of test specimen, and at end of culture, the colony counting was done. RESULTS AND

CONCLUSION:

In the bacterial adhesion test, the number of colonies of three kinds of bacteria in the experimental group was significantly lower than that in the control group (P<0.05). The number of bacterial adhesion in the control group was significantly higher than that in the experimental group. These findings indicate that the cobalt-chromium al oy covered with zirconium nitride coating can significantly reduce the adhesion amount of Streptococcus mutans, Candida albicans and Actinomyces viscosus, and thus improve bacterial adhesion properties of cobalt-chromium al oys.

Texto completo: DisponíveL Índice: WPRIM (Pacífico Ocidental) Idioma: Chinês Revista: Chinese Journal of Tissue Engineering Research Ano de publicação: 2015 Tipo de documento: Artigo

Similares

MEDLINE

...
LILACS

LIS

Texto completo: DisponíveL Índice: WPRIM (Pacífico Ocidental) Idioma: Chinês Revista: Chinese Journal of Tissue Engineering Research Ano de publicação: 2015 Tipo de documento: Artigo