Biocompatibility of poly-L-lactic acid/hydroxyapatite biomaterial with periodontal ligament cells / 中国组织工程研究
Chinese Journal of Tissue Engineering Research
;
(53): 1732-1737, 2016.
Artigo
em Chinês
| WPRIM
| ID: wpr-485685
ABSTRACT
BACKGROUND:
Hydroxyapatite/poly-L-lactic acid composite can wel improve the brittleness and mechanical properties of the hydroxyapatite.OBJECTIVE:
To study the biocompatibility of hydroxyapatite/poly-L-lactic acid composite biomaterials with periodontal ligament cels.METHODS:
Passage 4 human periodontal ligament cels at a density of 5×109/L were cultured with hydroxyapatite/poly-L-lactic acid composite as experimental group, and human periodontal ligament cels cultured alone as control group. Cel proliferation was detected within 7 days of culture; alkaline phosphatase activity was detected at 24, 48 and 72 hours of culture; and type I colagen expression was detected at 72 hours of culture. RESULTS ANDCONCLUSION:
There was no significant difference in the absorbance value of cels between the two groups at 1-7 days of culture. The alkaline phosphatase activity of cels at 48 and 72 hours was significantly higher than that at 24 hours (P < 0.05) in the two groups, but there was no difference between the two groups. The expression of type I colagen had no difference between the two groups. These findings indicate that the hydroxyapatite/poly-L-lactic acid composite biomaterial has good cel compatibility.
Texto completo:
DisponíveL
Índice:
WPRIM (Pacífico Ocidental)
Idioma:
Chinês
Revista:
Chinese Journal of Tissue Engineering Research
Ano de publicação:
2016
Tipo de documento:
Artigo
Similares
MEDLINE
...
LILACS
LIS