Effect Of Surface Treatments On The Bond Strength Of Denture Base Resins To Dental Alloy / 대한치과보철학회지
The Journal of Korean Academy of Prosthodontics
;
: 344-351, 2002.
Artigo
em Coreano
| WPRIM
| ID: wpr-49102
ABSTRACT
The purpose of this study is to compare tensile bond strength between Cr-Co alloy and three denture base resins after surface treatment. Following the manufacturer's instructions, 180 bonded specimens were made from three denture base resins (Lucitone 199, Paladent 20, POSS resin) and three surface treatment methods(sandblasting, metal primer, silicoating). 20 samples were made in each group and a half was thermocycled 1000 times between 5 celsius degrees and 55 celsius degrees. The tensile bond strength was measured using an Instron with 5mm/min crosshead speed. Data was analyzed with one-way ANOVA, T-test and Duncan test. The results were as follows 1. Samples with metal primer coating had significantly high tensile bond strength than the other surface treated groups (p.05). 3. Tensile bond strength was decreased in silicoated samples after thermocycling (p<.05). 4. Of the surface treated groups with metal primer,Lucitone 199 had the greatest bond strength and POSS resin and Paladent 20 were followed (p<.05). 5. Of the surface treated groups with silicoating, POSS resin and Lucitone 199 had greater bond strength than Paladent 20 (p<.05).
Texto completo:
DisponíveL
Índice:
WPRIM (Pacífico Ocidental)
Assunto principal:
Simulação por Computador
/
Dentaduras
/
Dióxido de Silício
/
Ligas Dentárias
/
Bases de Dentadura
/
Ligas
Idioma:
Coreano
Revista:
The Journal of Korean Academy of Prosthodontics
Ano de publicação:
2002
Tipo de documento:
Artigo
Similares
MEDLINE
...
LILACS
LIS