Preparation of chitosan/polyvinyl alcohol composite scaffold at different mass ratios:Comparison of structure and characteristics / 中国组织工程研究
Chinese Journal of Tissue Engineering Research
;
(53)2007.
Artigo
em Chinês
| WPRIM
| ID: wpr-596906
ABSTRACT
BACKGROUND:
Polyvinyl alcohol(PVA)has similar water content as human tissues,good biocompatibility and high mechanical strength,thereby being utilized as tissue-engineered matrix material.However,the modification in cellular affinity benefits the function as tissue regeneration scaffold materials.OBJECTIVE:
To prepare chitosan(CS)/PVA composite scaffold and explore the feasibility of serving as a scaffold for tissue engineering.METHODS:
Scaffolds of CS/PVA was fabricated by blending PVA-124 with various amounts of CS using film forming,particle forming,and free-drying methods.Water content,light transmittance,and swelling ratio were tested.Scanning electron microscope was used to observe the configuration of the cross section.RESULTS ANDCONCLUSION:
A total of 7 different proportional scaffolds were obtained with different PVA and CS dosage.The composite film showed light transmittance between 70%-80%,high water content between 121.2%-162.5% and swelling ratio between 60.3%-133.7%.Composite particle and sponge obtained water content between 82.0%-461.2% and 280.8%-1 939.0%.Composite scaffold with the amount ratio of PVA 0.75 g/CS 0.15 g exhibited the best performance.Scanning electron microscope showed that at a mass ratio of PVA 0.75 g/CS 0.15 g,the scaffold prepared by freeze-drying method had regular,fluffy inner structure,with good mechanics and high water content.
Texto completo:
DisponíveL
Índice:
WPRIM (Pacífico Ocidental)
Idioma:
Chinês
Revista:
Chinese Journal of Tissue Engineering Research
Ano de publicação:
2007
Tipo de documento:
Artigo
Similares
MEDLINE
...
LILACS
LIS