The effects of oxidation of titanium on the bonding strength of titanium and porcelain / 实用口腔医学杂志

ABSTRACT

Objective:To investigate the effects of oxidation of titanium on bonding strength of titanium and porcelain. Methods: 24 specimens with a size of 28 mm ?3 mm?0.5 mm were cast from pure titanium and divided into 4 groups, 6 specimens each group. Group 2, 3 and 4 were degassed at 750, 800 and 900 ℃ respectively, group 1 not degassed as negative control, then a uniform thickness of 1mm of Noritake super porcelain Ti-22 was veneered on 8 mm?3 mm in the central portion of each specimen. The specimens were subjected to a three-point bending test on a load-test machine with a span of 20 mm, and the failure loads were recorded and analyzed statistically. The opposite side of specimens of each group were observed by thin-film X-ray diffraction. Results: The failure loads (N) of group 1, 2, 3 and 4 were 10.33, 9.98, 5.53, 3.37. The oxide of group 1 was Ti6O only, the oxide of the gropu 2, 3, and 4 were Ti6O and TiO2 and the amount of TiO2 increased significantly as the temperature iss increasing. Conclusion: The oxide adherence strength value for pure titanium decreased while the oxide temperature is increasing. The higher of the degassed temperature of the specimens, the more TiO2 can be found in the oxide film and the smaller the failure load is, which indicats that oxidation of titanium has a negative effect on the bonding strength of porcelain and titanium.