In vitro evaluation of the wear resistance of provisional resin materials fabricated by different methods / 대한치과보철학회지
The Journal of Korean Academy of Prosthodontics
;
: 110-117, 2019.
Artigo
em Coreano
| WPRIM
| ID: wpr-742108
ABSTRACT
PURPOSE:
This study was to evaluate the wear resistance of 3D printed, milled, and conventionally cured provisional resin materials. MATERIALS ANDMETHODS:
Four types of resin materials made with different methods were examined Stereolithography apparatus (SLA) 3D printed resin (S3P), digital light processing (DLP) 3D printed resin (D3P), milled resin (MIL), conventionally self-cured resin (CON). In the 3D printed resin specimens, the build orientation and layer thickness were set to 0° and 100 µm, respectively. The specimens were tested in a 2-axis chewing simulator with the steatite as the antagonist under thermocycling condition (5 kg, 30,000 cycles, 0.8 Hz, 5℃/55℃). Wear losses of the specimens were calculated using CAD software and scanning electron microscope (SEM) was used to investigate wear surface of the specimens. Statistical significance was determined using One-way ANOVA and Dunnett T3 analysis (α = .05).RESULTS:
Wear losses of the S3P, D3P, and MIL groups significantly smaller than those of the CON group (P .05). In the SEM observations, in the S3P and D3P groups, vertical cracks were observed in the sliding direction of the antagonist. In the MIL group, there was an overall uniform wear surface, whereas in the CON group, a distinct wear track and numerous bubbles were observed.CONCLUSION:
Within the limits of this study, provisional resin materials made with 3D printing show adequate wear resistance for applications in dentistry.
Texto completo:
DisponíveL
Índice:
WPRIM (Pacífico Ocidental)
Assunto principal:
Técnicas In Vitro
/
Vestuário
/
Odontologia
/
Impressão Tridimensional
/
Mastigação
/
Métodos
Idioma:
Coreano
Revista:
The Journal of Korean Academy of Prosthodontics
Ano de publicação:
2019
Tipo de documento:
Artigo
Similares
MEDLINE
...
LILACS
LIS