Comparison analysis of fracture load and flexural strength of provisional restorative resins fabricated by different methods / 대한치과보철학회지
The Journal of Korean Academy of Prosthodontics
;
: 225-231, 2019.
Artigo
em Coreano
| WPRIM
| ID: wpr-761436
ABSTRACT
PURPOSE:
This study was undertaken to compare fracture and flexural strength of provisional restorative resins fabricated by additive manufacturing, subtractive manufacturing, and conventional direct technique. MATERIALS ANDMETHODS:
Five types of provisional restorative resin made with different methods were investigated Stereolithography apparatus (SLA) 3D printer (S3Z), two digital light processing (DLP) 3D printer (D3Z, D3P), milling method (MIL), conventional method (CON). For fracture strength test, premolar shaped specimens were prepared by each method and stored in distilled water at 37℃ for 24 hours. Compressive load was measured using a universal testing machine (UTM). For flexural strength test, rectangular bar specimens (25 × 2 × 2 mm) were prepared by each method according to ISO 10477 and flexural strength was measured by UTM.RESULTS:
Fracture strengths of the S3Z, D3Z, and D3P groups fabricated by additive manufacturing were not significantly different from those of MIL and CON groups (P>.05/10=.005). On the other hand, the flexural strengths of S3Z, D3P, and MIL groups were significantly higher than that of CON group (P<.05), but the flexural strength of D3Z group was significantly lower than that of CON group (P<.05).CONCLUSION:
Within the limitation of our study, provisional restorative resins made from additive manufacturing showed clinically comparable fracture and flexural strength as those made by subtractive manufacturing and conventional method.
Texto completo:
DisponíveL
Índice:
WPRIM (Pacífico Ocidental)
Assunto principal:
Dente Pré-Molar
/
Água
/
Impressão Tridimensional
/
Mãos
/
Métodos
Idioma:
Coreano
Revista:
The Journal of Korean Academy of Prosthodontics
Ano de publicação:
2019
Tipo de documento:
Artigo
Similares
MEDLINE
...
LILACS
LIS