The blocking effect and abrasion resistance of hydroxyapatite with different particle sizes and morphologies for dentinal tubules / 口腔疾病防治

ABSTRACT

Objective@#To study the blocking effect and abrasion resistance of hydroxyapatite (HA) with different particle sizes and morphologyies on dentinal tubules from the qualitative and quantitative aspects. @*Methods @# Dentin discs were etched and divided into 4 groups randomly: 20 nm HA group; 30 nm HA group; 12 μm HA group; control group (without any experimental treatment). Each group was brushed with correspondent materials for 7 days. Then, the dentin disk was divided into two parts, the one was detected by the scanning electron microscopy (SEM); the other was observed by SEM after toothbrush abrasion test. The Image-Pro Plus 6.0 image analysis software was used to calculate the plugging rate of dentinal tubules. @*Results @#SEM showed that the blockage is granular, the plugging rate of the dentinal tubules were about 82% to 96%. 30 nm HA group (short rod) range the first in the average plugging rate, followed by the 20 nm HA group (needles) and 12 μm HA group (spherical). After mechanical brushing for 7 days, SEM images showed that deposited layer in each group was smooth and compact, and more than 63% of the tubules still had been blocked. @* Conclusion @#HA with different particle sizes and morphologies had good plugging effect and abrasion resistance on dentine tubules. The blocking effect of HA was affected not only by particle size but also by the morphology.